Multibase Multi-FlexÂ® TPE A 5801 LC BLK

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer	Multibase
Trade Name	Multi-Flex® TPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-FlexÂ® TPE A 5801 LC BLK.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Multi-FlexÂ® LC compounds are a new generation elastomers exhibiting improved compression set at elevated temperature. Multi-FlexÂ® TPE compounds are based on Shell's Kraton G technology and feature excellent heat and ozone resistance. LC products cover a wide temperature span from -40Â°F to 300Â°F. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/inÂ³	ASTM D792
Melt Flow	1.0 g/10 min @Load 5.00 kg, Temperature 230 Â°C	1.0 g/10 min @Load 11.0 lb, Temperature 446 Â°F	ASTM D-1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	58	58	10 sec; ASTM D-2240
Tensile Strength, Ultimate	6.60 MPa	957 psi	ASTM D638
Elongation at Break	900 %	900 %	ASTM D638
100% Modulus	0.00280 GPa	0.406 ksi	ASTM D638
300% Modulus	0.00413 GPa	0.599 ksi	ASTM D638
Tear Strength	23.8 kN/m	136 pli	ASTM D624
Compression Set	12 %	12 %	for 70 hours at 23Â°C; ASTM 395
	34 % @Temperature 70.0 Â°C	34 % @Temperature 158 Â°F	for 70 hours at 70Â°C; ASTM 395
	42 % @Temperature 100 Â°C	42 % @Temperature 212 Â°F	70 hours at 100Â°C; ASTM 395