Ineos HB111R Polyethylene Copolymer

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer	Ineos Olefins & Polymers USA
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos HB111R Polyethylene Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HB111R is a natural high molecular weight, high-density copolymer polyethylene developed for automotive fuel tanks. It combines excellent processability and outstanding physical performance, particularly environmental stress crack resistance (ESCR) and impact properties. Its high melt strength aids the continuous extrusion production of multi-layer tanks.

Physical Properties	Metric	English	Comments
Density	0.945 g/cc	0.0341 lb/in³	ASTM D4883
Melt Flow	6.0 g/10 min @Load 21.6 kg, Temperature 190 °C	6.0 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	64	64	ASTM D2240
Tensile Strength, Yield	24.1 MPa	3500 psi	2 in/min; ASTM D638
Elongation at Break	800 %	800 %	2 in/min; ASTM D638
Flexural Modulus	0.820 GPa	119 ksi	2% Secant-Method 1; ASTM D790
Izod Impact, Notched	3.74 J/cm	7.00 ft-lb/in	Partial Break; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	70.0 °C	158 °F	ASTM D648
Vicat Softening Point	129 °C	264 °F	ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746