Hexcel® HexPly® F155 Epoxy Resin, 220 Glass Fabric

Category Polymer , Thermoset , Epoxy , Epoxy/Glass SMC
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F155 Epoxy Resin, 220 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 4.544 MPa

@Temperature 93.0 °C
 659.1 psi

@Temperature 199 °F
 Flatwise TS
5.509 MPa

@Temperature 71.0 °C
 799.0 psi

@Temperature 160 °F
 Flatwise TS
6.026 MPa

@Temperature 24.0 °C
 874.0 psi

@Temperature 75.2 °F
 Flatwise TS
330 MPa

@Temperature 93.0 °C
 47900 psi

@Temperature 199 °F
363 MPa

@Temperature 71.0 °C
 52600 psi

@Temperature 160 °F
416 MPa

@Temperature 24.0 °C
 60300 psi

@Temperature 75.2 °F
Tensile Modulus 17.9 GPa

@Temperature 93.0 °C
 2600 ksi

@Temperature 199 °F
18.6 GPa

@Temperature 71.0 °C
 2700 ksi

@Temperature 160 °F
20.7 GPa

@Temperature 24.0 °C
 3000 ksi

@Temperature 75.2 °F
Compressive Yield Strength 341 MPa

@Temperature 93.0 °C
 49500 psi

@Temperature 199 °F
376 MPa

@Temperature 71.0 °C
 54500 psi

@Temperature 160 °F
496 MPa

@Temperature 24.0 °C
 71900 psi

@Temperature 75.2 °F
Compressive Modulus 18.6 GPa

@Temperature 93.0 °C
 2700 ksi

@Temperature 199 °F
20.7 GPa

@Temperature 71.0 °C
 3000 ksi

@Temperature 160 °F
22.1 GPa

@Temperature 24.0 °C
 3210 ksi

@Temperature 75.2 °F
Shear Strength 63.0 MPa
9140 psi
Compression interlaminar; RT
43.0 MPa

@Temperature 93.0 °C
 6240 psi

@Temperature 199 °F
 Compression interlaminar
53.0 MPa

@Temperature 71.0 °C
 7690 psi

@Temperature 160 °F
 Compression interlaminar