ExxonMobil LLDPE LL 1004YB Film Linear Low Density Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer	Exxon Chemical
Trade Name	LLDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LLDPE LL 1004YB Film Linear Low Density Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LL 1004YB is an LLDPE grade, offering excellent high temperature stability. Properties may be further enhanced by the combination with Exceed mLLDPE. Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications: Cast FilmCast Stretch FilmFood packagingForm Fill and Seal PackagingGeneral PackagingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ExxonMobil method
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 190 °C	2.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	810 %	810 %	ASTM D882
Elmendorf Tear Strength MD	40 g	40 g	ASTM D1922
Elmendorf Tear Strength TD	500 g	500 g	ASTM D1922
Dart Drop Test	60.0 g	0.132 lb	ASTM D1709A
Film Tensile Strength at Break, MD	50.3 MPa	7300 psi	ASTM D882
Film Tensile Strength at Break, TD	24.1 MPa	3500 psi	ASTM D882
1% Secant Modulus, MD	117 MPa	17000 psi	ASTM D882
1% Secant Modulus, TD	138 MPa	20000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 250 °C	<= 482 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	1.5 %	1.5 %	ASTM D1003
Gloss	93 %	93 %	45°; ASTM D2457