Eastman D4032-F Polyethylene (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman D4032-F Polyethylene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
D4032-F is a low density, fractional-melt formulation which contains no slip and medium antiblock. It is designed for film applications requiring exceptional toughness, such as in heavy-duty shipping sacks or in construction and agricultural films.Information supplied by the manufacturer.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D4883 |
| Thickness | 76.0 microns | 2.99 mil | |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 320 % | 320 % | ASTM D882 |
| Film Elongation at Break, TD | 885 % | 885 % | ASTM D882 |
| Secant Modulus, MD | 0.193 GPa | 28.0 ksi | 1% Secant; ASTM D882 |
| Secant Modulus, TD | 0.231 GPa | 33.5 ksi | 1% Secant; ASTM D882 |
| Elmendorf Tear Strength MD | 355 g | 355 g | |
| Elmendorf Tear Strength TD | 334 g | 334 g | |
| Elmendorf Tear Strength, MD | 4.66 g/micron | 118 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.33 g/micron | 110 g/mil | ASTM D1922 |
| Dart Drop | 4.19 g/micron | 106 g/mil | ASTM D1709A |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 53 % | 53 % | at 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Film |