- Dow DOWLEX™ 2038 Linear Low Density Polyethylene
Dow DOWLEX™ 2038 Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2038 Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Linear Low Density PolyethyleneInformation provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Melt Index of Compound | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 15.23 MPa | 2209 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.72 MPa | 2425 psi | ASTM D882 |
| Film Elongation at Break, MD | 522 % | 522 % | ASTM D882 |
| Film Elongation at Break, TD | 656 % | 656 % | ASTM D882 |
| Secant Modulus, MD | 0.377 GPa | 54.7 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.348 GPa | 50.5 ksi | 2% Secant; ASTM D882 |
| Elmendorf Tear Strength, MD | 2.80 g/micron | 71.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.3 g/micron | 413 g/mil | ASTM D1922 |
| Dart Drop Test | 112 g | 0.247 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 38.34 MPa | 5561 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.13 MPa | 4805 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 126 °C | 259 °F | Dow Method |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; ASTM D2457 |