Chevron Phillips Marlex® H516HP High Density Polyethylene, Pressure Pipe Grade

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer Chevron Phillips Chemical Company LP
Trade Name Marlex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Marlex® H516HP High Density Polyethylene, Pressure Pipe Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This high performance PE 4710 HDPE is tailored for the demands of pressure pipe applications that require:Excellent long-term hoop strengthSuperb resistance to slow crack growthExceptional resistance to rapid crack propagationOutstanding low-temperature toughnessAdditional InformationMeets ASTM D4796 - PE 235NSF Third party D2513 certifiedNSF CSA B137.1 and B137.4 certifiedTypical applications for H516HP include:Gas distributionPotable waterIndustrialWhen blended with an approved black concentrate, the material meets or exceeds:ASTM D3350, class 445574C and 445576CNSF Standards 14 and 61 for potable waterPPI designations PE 4710 and PE 100Information provided by Chevron Phillips Chemical Company LP.
Physical Properties Metric English Comments
Specific Gravity 0.949 g/cc
0.949 g/cc
ASTM D1505
Melt Flow 9.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
9.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
PENT >= 10000 hour
>= 10000 hour
ASTM F1473
Tensile Strength, Yield 25.5 MPa
3700 psi
2 in/min, Type IV bar; ASTM D638
Elongation at Break >= 700 %
>= 700 %
2 in/min, Type IV bar; ASTM D638
Flexural Modulus 0.965 GPa
140 ksi
2% Secant; ASTM D790
Hydrostatic Design Basis 6.90 MPa

@Temperature 60.0 °C
1000 psi

@Temperature 140 °F
ASTM D2837
11.0 MPa

@Temperature 23.0 °C
1600 psi

@Temperature 73.4 °F
ASTM D2837
Descriptive Properties Value Comments
Minimum Required Strength 10.0 MPa
ISO 9080
Notched Pipe Test 500 h
ISO 13479, 80°C
Rapid Crack Propagation 12 bar
ISO 13477, 0°C