Material Notes:
Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy is produced by vacuum induction melting (VIM) followed by electroslag remelting (ESR).BioDur™ and Carpenter CCM® are trademarks of Carpenter Technology Corporation.
Physical Properties Metric English Comments
Density 8.287 g/cc
0.2994 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 369
369
Estimated from Rockwell C for Brinell test with 3000 kg load, 10 mm ball.
Hardness, Knoop 403
403
Estimated from Rockwell C
Hardness, Rockwell C 40
40
Hardness, Vickers 386
386
Estimated from Rockwell C
Tensile Strength, Ultimate 1310 MPa
190000 psi
Tensile Strength, Yield 930 MPa

@Strain 0.200 %
135000 psi

@Strain 0.200 %
Elongation at Break 26 %
26 %
in 4D
Reduction of Area 23 %
23 %
Thermal Properties Metric English Comments
CTE, linear 13.18 µm/m-°C

@Temperature 0.000 - 100 °C
7.322 µin/in-°F

@Temperature 32.0 - 212 °F
13.47 µm/m-°C

@Temperature 25.0 - 300 °C
7.483 µin/in-°F

@Temperature 77.0 - 572 °F
15.09 µm/m-°C

@Temperature 25.0 - 700 °C
8.383 µin/in-°F

@Temperature 77.0 - 1290 °F
17.08 µm/m-°C

@Temperature 25.0 - 1150 °C
9.489 µin/in-°F

@Temperature 77.0 - 2100 °F
Specific Heat Capacity 0.470 J/g-°C

@Temperature 23.0 °C
0.112 BTU/lb-°F

@Temperature 73.4 °F
0.590 J/g-°C

@Temperature 600 °C
0.141 BTU/lb-°F

@Temperature 1110 °F
0.673 J/g-°C

@Temperature 1100 °C
0.161 BTU/lb-°F

@Temperature 2010 °F
Thermal Conductivity 12.66 W/m-K

@Temperature 23.0 °C
87.86 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
25.76 W/m-K

@Temperature 600 °C
178.8 BTU-in/hr-ft²-°F

@Temperature 1110 °F
35.57 W/m-K

@Temperature 1177 °C
246.9 BTU-in/hr-ft²-°F

@Temperature 2151 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.10 %
<= 0.10 %
Chromium, Cr 26 - 30 %
26 - 30 %
Cobalt, Co 62 %
62 %
as remainder
Iron, Fe <= 0.75 %
<= 0.75 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Molybdenum, Mo 5.0 - 7.0 %
5.0 - 7.0 %
Nickel, Ni <= 1.0 %
<= 1.0 %
Nitrogen, N <= 0.25 %
<= 0.25 %
Silicon, Si <= 1.0 %
<= 1.0 %