Polymer Property : Tensile Strength, Ultimate = 1310 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1310 - 1520 MPa	190000 - 220000 psi
Materion Beryllium Copper Alloy 25 Strip; HT (TH04) Temper (UNS C17200) Treatment required for max strength: 2 hrs @ 315ÂºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 98%Stress Relaxation after 1000 hrs @ 200Â°C: 74%Superficial Hardness: 30N 58-6..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Typical
Industeel VIRGO 17.4PH 17Cr-4Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (496Â°C - 4 hours + air cooled) Description: Alloy VIRGO 17.4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 300Â°C / 572Â°F) and corr..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Typical
Industeel VIRGO 15.5PH 15Cr-5Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (496Â°C - 4 hours - air cooling) Description: Alloy VIRGO 15.5 PH is a precipitation hardening martensitic stainless steel with 15% Cr, 5% Ni, 3.5% Cu and 0.3% Nb/Cb. The grade combines high mechanical properties and medium corrosi..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Tempered at 900Â°F, 1hr
Latrobe LescalloyÂ® 15-5 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 15-5 VAC-ARC steel is a precipitation hardening martensitic stainless steel commonly considered to be a compositional modification of 17-4 with minimal delta ferrite. A wide range of mec..
Tensile Strength, Ultimate	>= 1310 MPa	>= 190000 psi	H900 Condition - 480Â°C at 1 hr
Latrobe LescalloyÂ® 15-5 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 15-5 VAC-ARC steel is a precipitation hardening martensitic stainless steel commonly considered to be a compositional modification of 17-4 with minimal delta ferrite. A wide range of mec..
Tensile Strength, Ultimate	>= 1310 MPa	>= 190000 psi	H900 Condition - 480Â°C at 1 hr
Latrobe LescalloyÂ® 17-4 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Tensile Strength, Ultimate	1310 MPa	190000 psi
Latrobe LescalloyÂ® HY-180 VIM-VAR ; .375 - 2 thickness High Strength Alloy Steel LESCALLOY HY-180 VIM-VAR steel is a high strength alloy steel with superior toughness. It is double vacuum melted (VIM-VARâ€¦vacuum induction melted followed by vacuum arc remelting) to provide s..
Tensile Strength, Ultimate	1310 - 1590 MPa	190000 - 231000 psi
Materion Beryllium Copper Alloy M25 Wire; 3/4HT (TH03) Temper; 1.3-2.0 mm Diameter (UNS C17300) Treatment required for max strength: 1 hr @ 315-330Â°C Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed it..
Tensile Strength, Ultimate	1310 - 1550 MPa	190000 - 225000 psi	Core; Heat Treated from 1850Â°F
Latrobe CBS-223â„¢ VIM-VAR Carburizing Bearing and Gear Steel CBS-223 VIM-VAR steel is a double vacuum melted carburizing steel with high hot hardness characteristics. Double vacuum melting sequentially combines vacuum induction melting with VACARCâ„¢ remel..
Tensile Strength, Ultimate	1310 MPa	190000 psi
Latrobe LescalloyÂ® HY-180 VIM-VAR ; 2.01 - 4.00 thickness High Strength Alloy Steel LESCALLOY HY-180 VIM-VAR steel is a high strength alloy steel with superior toughness. It is double vacuum melted (VIM-VAR vacuum induction melted followed by vacuum arc remelting) to provide superi..
Tensile Strength, Ultimate	1310 - 1370 MPa	190000 - 199000 psi
Latrobe LescalloyÂ® Jethete M-152 ESR 3" RD High Strength Stainless Steel LESCALLOY JETHETE M-152 ESR is a nitrogen bearing, hardenable 12% chromium stainless steel intended for various structural components requiring high strength and good oxidation resistance up to 800Â..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Typical
TIMET TIMETAL® 21S Titanium Alloy (Ti-15Mo-3Nb-3Al-0.2Si, ASTM Grade 21); Aged at 538°C High-Strength, Oxidation Resistant Strip AlloyFeatures: Offers the good cold formability and weldability of a beta strip alloy, but with greatly improved oxidation resistance and creep strength. Aer..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Typical
TIMET TIMETAL® 551 (Ti-4Al-4Mo-4Sn-0.5Si) Titanium Alloy; 25-100 mm High-Strength Forging AlloyIndustry Specifications: UK Aerospace Specifications BS TA.38, 39, 40, 41, 42.Features: TIMETAL 551 has high strength and is creep resistant up to 400°C. It has a simila..
Tensile Strength, Ultimate	1310 MPa @Temperature 20.0 °C	190000 psi @Temperature 68.0 °F	Age hardened at 42 HRC
EDRO UltraChem® #15 Precipitation Hardening Stainless Mold Steel Ultrachem® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by: exceptional corrosion resistance, uniform hardness in all dimensions, ..
Tensile Strength, Ultimate	1310 MPa @Temperature 20.0 °C	190000 psi @Temperature 68.0 °F	Age hardened at 42 HRC
EDRO UltraChem® ESR #16 Precipitation Hardening Stainless Mold Steel Ultrachem ESR® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by exceptional polishability, exceptional corrosion resistance, unifor..
Tensile Strength, Ultimate	1310 MPa	190000 psi
Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi..
Tensile Strength, Ultimate	1310 MPa	190000 psi
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 2 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h..
Tensile Strength, Ultimate	1310 MPa	190000 psi
Carpenter BioDur™ CCM® Medical Implant Alloy, Warm Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy..
Tensile Strength, Ultimate	1310 MPa	190000 psi
Carpenter Custom 450® Stainless Steel, 25 mm Bar, Condition H1050 (Age Hardened 566°C) Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T..
Tensile Strength, Ultimate	1310 MPa @Temperature 260 °C	190000 psi @Temperature 500 °F
Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good ..
Tensile Strength, Ultimate	1310 MPa	190000 psi
ATI Allvac® Nickelvac® 80 A UNS N07080 Nickel Superalloy Uses: Components for gas turbine engines, exhaust valve stock for internal combustion engines, high temperature bolts & fasteners.Property values are for samples in the metallurgical condition: 1700..
Tensile Strength, Ultimate	1310 MPa	190000 psi
ATI Allvac® Nickelvac® X- 751 UNS N07751 Nickel Superalloy Uses: Components for gas turbine engines, exhaust valve stock for internal combustion engines.Property values are for samples in the metallurgical condition: 1800°F age.Information provided by Allv..
Tensile Strength, Ultimate	1310 MPa	190000 psi
ATI Allvac® 520 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) + Age Data provided by Allvac.Applications: Land based gas turbine blades.
Tensile Strength, Ultimate	1310 MPa	190000 psi
Latrobe Lescalloy® HY-180 VIM-VAR ; 4.01 - 8.00 thickness High Strength Alloy Steel LESCALLOY HY-180 VIM-VAR steel is a high strength alloy steel with superior toughness. It is double vacuum melted (VIM-VAR vacuum induction melted followed by vacuum arc remelting) to provide superi..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Oil Quenched from 871°C; 649°C Temper Temperature
Latrobe Staminal™ Shock Resisting Die Steel Staminal is an air or oil hardening die steel containing a large percentage of nickel combined with a proper balance of other alloying elements for deep hardening and extreme toughness. For tools, ..
Tensile Strength, Ultimate	>= 1310 MPa	>= 190000 psi
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H775 (H775) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
Tensile Strength, Ultimate	1310 - 1590 MPa	190000 - 231000 psi
Materion Beryllium Copper Alloy 25 Wire; 3/4HT (TH03) Temper; 1.3-2.0 mm Diameter (UNS C17200) Treatment required for max strength: 1 hr @ 315-330°C Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its ..
Tensile Strength, Ultimate	1310 MPa	190000 psi	Precipitation Hardened
Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a..