Braskem FL31 LLDPE Cast Film Extrusion Polyethylene Copolymer

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem FL31 LLDPE Cast Film Extrusion Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FL31 is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process. It was developed for cast film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties. It contains processing aid and antioxidant additives. Its applications include: stretch films, liners, LDPE and HDPE blends, and packages for general use. Recommended processing conditions for film extrusion are about 220 - 270 ºC.
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM-D792
Melt Flow 2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 1100 %
1100 %
ASTM-D882
Film Elongation at Break, TD 1380 %
1380 %
ASTM-D882
Elmendorf Tear Strength MD 100 g
100 g
ASTM-D1922
Elmendorf Tear Strength TD 290 g
290 g
ASTM-D1922
Elmendorf Tear Strength, MD 4.00 g/micron
102 g/mil
ASTM-D1922
Elmendorf Tear Strength, TD 11.6 g/micron
295 g/mil
ASTM-D1922
Dart Drop 4.00 g/micron
102 g/mil
ASTM-D1709
Dart Drop Test 100 g
0.221 lb
ASTM-D1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM-D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM-D882
1% Secant Modulus, MD 140 MPa
20300 psi
ASTM-D882
1% Secant Modulus, TD 150 MPa
21800 psi
ASTM-D882
Optical Properties Metric English Comments
Haze 35 %
35 %
ASTM-D1003
Gloss 52 %
52 %
Angle 60°; ASTM-D2457