Polymer Property : Volume Resistivity = 1.00e+13 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm @Temperature 23.0 °C	1.00e+13 ohm-cm @Temperature 73.4 °F	50%RH; IEC 60093
DuPont Performance Polymers Zytel® E51HSB NC010 Nylon 66 (Unverified Data**) Zytel® E51HSB NC010 is a high molecular weight, heat stabilized polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Volume Resistivity	1.00e+13 ohm-cm @Temperature 250 Â°C	1.00e+13 ohm-cm @Temperature 482 Â°F
Schott Glass 8240 Alkaline Earth Aluminosilicate Glass Alkaline earth aluminosilicate glass for high temperature application in electrical engineering, for sealing to molybdenum, free from alkali, blue colored, defined absorption Bulb and exhaust tube ..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 250 Â°C	1.00e+13 ohm-cm @Temperature 482 Â°F
Schott Glass 8253 Alkaline Earth Aluminosilicate Glass Alkaline earth aluminosilicate glass for high temperature application in electrical engineering, for sealing to molybdenum, for use at higher temperatures than glass 8252, free from alkali Bulb and..
Volume Resistivity	>= 1.00e+13 ohm-cm @Temperature 20.0 Â°C	>= 1.00e+13 ohm-cm @Temperature 68.0 Â°F
Sibur 1030-13 Compound OMN Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p..
Volume Resistivity	>= 1.00e+13 ohm-cm @Temperature 20.0 Â°C	>= 1.00e+13 ohm-cm @Temperature 68.0 Â°F
Sibur 140-13 Compound 230/1 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 100 °C	1.00e+13 ohm-cm @Temperature 212 °F	IEC 672-1
CeramTec Frequenta® Steatite Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. Frequenta® has low dielectric loss, but has be..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 25.0 °C	1.00e+13 ohm-cm @Temperature 77.0 °F	ASTM-D257
CeramTec Rubalit® 708S Alumina, 96% Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 25.0 °C	1.00e+13 ohm-cm @Temperature 77.0 °F	ASTM-D257
CeramTec Rubalit® 710 Alumina, 99.6% Rubalit® 710 (99.6%) is an alumina that produces optimum results and is considered the material of choice for thin-film technology. Its characterizing features are high strength and thermal conduct..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 500 °C	1.00e+13 ohm-cm @Temperature 932 °F
CeramTec Rubalit® 710 Alumina, 99.6% Rubalit® 710 (99.6%) is an alumina that produces optimum results and is considered the material of choice for thin-film technology. Its characterizing features are high strength and thermal conduct..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 400 °C	1.00e+13 ohm-cm @Temperature 752 °F	IEC 672-1
CeramTec V 679 Alumina, 99.7% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures.
Volume Resistivity	>= 1.00e+13 ohm-cm @Temperature 25.0 °C	>= 1.00e+13 ohm-cm @Temperature 77.0 °F	ASTM-D1829
CoorsTek ADS-995R MidFilm™ 99.5% Alumina Thick Film Applications: thick films and lasers
Volume Resistivity	>= 1.00e+13 ohm-cm @Temperature 25.0 °C	>= 1.00e+13 ohm-cm @Temperature 77.0 °F	ASTM D1829
CoorsTek Hot Pressed Aluminum Nitride Aluminum Nitride Advantages: High heat dissipation with thermal conductivity of 170 W/m K Non-toxic alternative to BeO Thermal expansion coefficient similar to Si, GaN, and GaAs semiconductors H..
Volume Resistivity	>= 1.00e+13 ohm-cm @Temperature 300 °C	>= 1.00e+13 ohm-cm @Temperature 572 °F	ASTM-D257
CoorsTek Superstrate® 996 99.6% Alumina Thin Film Applications: thin film substrates
Volume Resistivity	1.00e+13 ohm-cm @Temperature 30.0 °C	1.00e+13 ohm-cm @Temperature 86.0 °F	JIS-K-6723
Denka VINYKON W7080 PVC, W grade for non-migratory sheath and special items A PVC resin compound offering excellent physical properties and workability. A broad product lineup is available, including hard and soft grades, as well as those for extrusion and injection molding..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 20.0 °C	1.00e+13 ohm-cm @Temperature 68.0 °F
Anderman Ceramics EZY 94 Zirconia, 94%, Yttria-Stabilized Dense impervious zirconia for high wear and aggressive engineering applications. Available in many shapes and sizes.Information provided by Anderman Ceramics.
Volume Resistivity	1.00e+13 ohm-cm @Temperature 100 °C	1.00e+13 ohm-cm @Temperature 212 °F	ASTM D257
3M Scotchcast™ 265 Electrical Epoxy Powder Resin 3M Scotchcast Electrical Resin 265 is a new solution to an old problem. Historically, manufactures of coils, stators and armatures have used liquid-based varnishes or resins to coat and impregnate t..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 23.0 °C	1.00e+13 ohm-cm @Temperature 73.4 °F	50%RH; IEC 60093
DuPont Performance Polymers Zytel® ST801 NC010A Nylon 66 (Unverified Data**) Zytel® ST801 is an unreinforced, super tough polyamide 66 for injection molding and extrusion. It offers outstanding break resistance over a wide temperature and humidity range and high productivit..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 20.0 °C	1.00e+13 ohm-cm @Temperature 68.0 °F
Anderman Ceramics EZM 96 Zirconia, 96.5%, Magnesia-Stabilized Zirconia materials offer high temperature capability as well as excellent performance in areas of high wear and corrosion. Available in many shapes and sizes.
Volume Resistivity	1.00e+13 ohm-cm @Temperature 100 °C	1.00e+13 ohm-cm @Temperature 212 °F	IEC 672-1
CeramTec 447 Cordierite, 2MgO•Al2O3•5SiO2 Cordierites have low coefficients of thermal expansion and excellent resistance to thermal shock. They offer a range of thermal expansion, mechanical strength, and porosity criteria. They excel as c..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 20.0 °C	1.00e+13 ohm-cm @Temperature 68.0 °F	ASTM-D257
CeramTec CeramCool® Rubalit® 708 Alumina, 96% CeramCool® is a metallized ceramic heat-sink for high power applications demonstrated by high power LED-systems. CeramCool® material characteristics: electrical insulation, high volume resistivit..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 20.0 °C	1.00e+13 ohm-cm @Temperature 68.0 °F	IEC 345
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance) Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 250 °C	1.00e+13 ohm-cm @Temperature 482 °F
Schott Glass 8241 Alkaline Earth Aluminosilicate Glass Alkaline earth aluminosilicate glass for high temperature application in electrical engineering, for sealing to molybdenum, free from alkali, blue colored, defined absorption Bulb and exhaust tube ..
Volume Resistivity	1.00e+13 ohm-cm @Temperature 20.0 °C	1.00e+13 ohm-cm @Temperature 68.0 °F
Anderman Ceramics EZY 88 Zirconia, 88%, Fully Yttria-Stabilized Zirconia materials offer high temperature capability as well as excellent performance in areas of high wear and corrosion. Available in many shapes and sizes.