- Polymer Property : Insulation Resistance = 1.00e+10 ohm
Polymer Property : Insulation Resistance = 1.00e+10 ohm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | 1.00e+10 - 1.00e+14 ohm | 1.00e+10 - 1.00e+14 ohm | Average value: 4.50e+12 ohm Grade Count:28 |
| Overview of materials for Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler". Specific grades with glass content between 5% .. |
|||
| Insulation Resistance | 1.00e+10 - 1.00e+11 ohm @Temperature 90.0 - 90.0 °C |
1.00e+10 - 1.00e+11 ohm @Temperature 194 - 194 °F |
Average value: 7.75e+10 ohm Grade Count:8 |
| Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini.. |
|||
| Insulation Resistance | <= 1.00e+10 ohm | <= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 1105-7916 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.High chemical resistance parts, hydrolysis resi.. |
|||
| Insulation Resistance | <= 1.00e+10 ohm | <= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 1105-8264 PEEK, with CNT Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect.. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 3-8266 Polyamide 6, unreinforced Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduce.. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 3-8277 Polyamide 6, unreinforced Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduce.. |
|||
| Insulation Resistance | <= 1.00e+10 ohm | <= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 80-7653 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Antistatic.No change of electric potential at bearings in case of separation of charge caused b.. |
|||
| Insulation Resistance | <= 1.00e+10 ohm | <= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® TPI-0953 Thermoplastic polyimide, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, apparatus- and precision engineering medical- and electrical enineering, aircraft- and aerospace industry.Very high continuous use and heat dist.. |
|||
| Insulation Resistance | <= 1.00e+10 ohm | <= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 1105-7916-1 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.High chemical resistance parts, hydrolysis resi.. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 1-7180/EG Polyamide 66, with carbon fiber, PTFE, lubricant modified, high viscosity, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Insulation Resistance | 1.00e+10 ohm @Temperature 90.0 °C |
1.00e+10 ohm @Temperature 194 °F |
IEC 60167 |
| Solvay Specialty Polymers Ryton® BR111 Polyphenylene Sulfide (PPS), GlassMineral Filled Ryton® BR111 is a natural-colored glass fiber and mineral filled polyphenylene sulfide compound that provides enhanced mechanical strength with good electrical properties and outstanding chemical.. |
|||
| Insulation Resistance | 1.00e+10 - 1.00e+11 ohm | 1.00e+10 - 1.00e+11 ohm | Dry; IEC 167 |
| Vyncolit 2923 W Novolac Phenolic Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
| Insulation Resistance | 1.00e+10 ohm | 1.00e+10 ohm | Wet; 24 hours in water; IEC 167 |
| Vyncolit 4523 XB Novolac Phenolic Organic and inorganic filled phenolic molding compound with good mechanical and thermal properties. Improved heat resistance compared to organic filled compounds.USES: Fuse holders, brush holders, .. |
|||
| Insulation Resistance | 1.00e+10 - 1.00e+11 ohm | 1.00e+10 - 1.00e+11 ohm | Dry; IEC 167 |
| Vyncolit 2920 W Novolac Phenolic Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B.. |
|||
| Insulation Resistance | 1.00e+10 ohm @Temperature 90.0 °C, Time 173000 sec |
1.00e+10 ohm @Temperature 194 °F, Time 48.0 hour |
95% RH |
| Chevron Phillips Xtel® XE3035BL Polyphenylene Sulfide Alloy Xtel® XE3035BL is a high performance, glass fiber reinforced, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information p.. |
|||
| Insulation Resistance | 1.00e+10 ohm @Temperature 90.0 °C, Time 173000 sec |
1.00e+10 ohm @Temperature 194 °F, Time 48.0 hour |
95% RH |
| Chevron Phillips Xtel® XE3035NA Polyphenylene Sulfide Alloy Xtel® XE3035NA is a high performance, glass fiber reinforced, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information p.. |
|||
| Insulation Resistance | 1.00e+10 ohm @Diameter 8.00 - 10.0 mm |
1.00e+10 ohm @Diameter 0.315 - 0.394 in |
24hr/50°C+24h in water at 23°C; IEC; IEC/EN 61212-2 6.2 |
| Elektro-Isola G-Etronax EP 11 Epoxy, Glass Fabric Reinforcement, Green, Tubes Description: Particularly good electrical and mechanical properties. Extremely high mechanical strength, even at high temperatures. Retains electrical properties at high air humidity. High resistanc.. |
|||
| Insulation Resistance | 1.00e+10 ohm @Diameter 8.00 - 10.0 mm |
1.00e+10 ohm @Diameter 0.315 - 0.394 in |
24hr/50°C+24h in water at 23°C; IEC; IEC/EN 61212-2 6.2 |
| Elektro-Isola G-Etronax EP 22 Epoxy, Glass Fabric Reinforcement, Light Yellow, Tubes Description: Particularly good electrical and mechanical properties. Extremely high mechanical strength, even at high temperatures. Retains electrical properties at high air humidity. High resistanc.. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | After immersion in water; IEC 1212-2 6.3 |
| Hippe EP CP 201 Cellulose Paper Reinforced Epoxy Resin - Sheet Used in electronic applications. Good stability of electrical properties under high humidity. Flame retardant.Information provided by Hippe. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | After immersion in water; IEC 1212-2 6.3 |
| Hippe PF CP 204 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in electrical and electronic applications. Good stability of electrical properties under high humidity. Also available in cold or hot-punching versions.Information provided by Hippe. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | After immersion in water; IEC 1212-2 6.3 |
| Hippe SI GC 201 Woven Glass Cloth Reinforced Silicone Resin - Sheet Used in electrical and electronic applications. Extremely good electrical properties under dry conditions; good properties under humid conditions.Information provided by Hippe. |
|||
| Insulation Resistance | 1.00e+10 ohm | 1.00e+10 ohm | After Boiling; ASTM D257 |
| Chang Chun Plastic Longlite PM T310 Impact Phenolic Molding Compound ASTM Grade per ASTM D700 is 13.Information provided by Dowell Trading Company Ltd. |
|||
| Insulation Resistance | 1.00e+10 ohm | 1.00e+10 ohm | Normal; ASTM D257 |
| Chang Chun Plastic Longlite PM T359J General Purpose Phenolic Molding Compound ASTM Grades per ASTM D700 are 3, 14.Information provided by Dowell Trading Company Ltd. |
|||
| Insulation Resistance | 1.00e+10 ohm | 1.00e+10 ohm | Normal; ASTM D257 |
| Chang Chun Plastic Longlite PM T373J Electrical Phenolic Molding Compound ASTM Grades per ASTM D700 are 2, 3.Information provided by Dowell Trading Company Ltd. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | (test voltage = 100 VDC; Mil-I-46058C |
| 3M 467MP High Performance Adhesive Transfer Tapes with Adhesive 200MP 3M™ High Performance Acrylic Adhesive 200MP is a popular choice for graphic attachment and membrane switch applications because it has excellent quality, consistency and durability. In addition, as.. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | (test voltage = 100 VDC; Mil-I-46058C |
| 3M 467MP High Performance Adhesive Transfer Tapes with Adhesive 200MP 3M™ High Performance Acrylic Adhesive 200MP is a popular choice for graphic attachment and membrane switch applications because it has excellent quality, consistency and durability. In addition, as.. |
|||
| Insulation Resistance | 1.00e+10 ohm | 1.00e+10 ohm | Normal; ASTM D257 |
| Chang Chun Plastic Longlite PM T385J General Purpose Phenolic Molding Compound ASTM Grades per ASTM D700 are 2, 3.Information provided by Dowell Trading Company Ltd. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 1301-8305 PPS, linear, with glass fiber, lubricant modified Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.Improved friction and wear behaviour. Emergency running property.Inherent flam.. |
|||
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Lehmann & Voss LUVOCOM® 1-8227 Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||