Polymer Property : Cure Time = 20.0 min Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	10.0 - 20.0 min	0.167 - 0.333 hour	On steel (Fixture)
ND Industries 530 Shaft & Bearing Retainer Retaining Compound General DescriptionA high strength adhesive for retention of cylindrical components, where disassembly is not required.Typical Usesrotors, shafts, bushings, bearings, and pulleysMeets military spec ..
Cure Time	5.00 - 20.0 min	0.0833 - 0.333 hour	for compression molded lab sheets
TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber Millathane 28 has excellent resistance to gas (e.g., nitrogen) permeability as well as very good abrasion resistance and low temperature properties. This polyurethane rubber was designed for automot..
Cure Time	15.0 - 20.0 min	0.250 - 0.333 hour	Working time
ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive II, Straw, Black Information provided by ITW Devcon
Cure Time	15.0 - 20.0 min	0.250 - 0.333 hour	Fixture time
ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive SD, Off-White Information provided by ITW Devcon
Cure Time	15.0 - 20.0 min	0.250 - 0.333 hour	Tack-free time
Master Bond MasterSil 705S Silver Filled, Non-Corrosive Silicone Description: Master Bond MasterSil 705S is an easy-to-use, one component, non-corrosive, electrically conductive, silver filled, silicone for bonding and sealing. The material is a gray colored past..
Cure Time	15.0 - 20.0 min	0.250 - 0.333 hour	Tack-free time
Master Bond MasterSil 709 One Part Silicone Meets MIL Spec Description: MasterSil 709 is an easy to use, one component, high performance silicone elastomer compound for bonding, sealing, coating and formed in place gaskets. This unique product meets the MIL..
Cure Time	5.00 - 20.0 min	0.0833 - 0.333 hour	for compression molded lab sheets
TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber Millathane 28 has excellent resistance to gas (e.g., nitrogen) permeability as well as very good abrasion resistance and low temperature properties. This polyurethane rubber was designed for automot..
Cure Time	15.0 - 20.0 min	0.250 - 0.333 hour	Time to Handling Strength
3M Scotch-Weld™ DP605NS Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-part, non-sag urethane adhesives. They feature tough, flexible bonds with good adhesion to a wide variety of substrates especially wood and many properl..
Cure Time	10.0 - 20.0 min	0.167 - 0.333 hour	Time to Handling Strength
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Cure Time	10.0 - 20.0 min	0.167 - 0.333 hour	Time to Handling Strength
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Cure Time	10.0 - 20.0 min	0.167 - 0.333 hour	Time to Handling Strength
3M Scotch-Weld™ DP100 FR Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP100 FR is a two-part flame retardant (self-extinguishing) version of Scotch-Weld DP100. It meets the UL94 V-O Burn Test requirements and has a work life of 4-8 mi..
Cure Time	15.0 - 20.0 min @Temperature 24.0 °C	0.250 - 0.333 hour @Temperature 75.2 °F
BCC Products BC 4570 Polyester Hi Heat Filler BC 4570 is a multi-purpose paste designed for making quick repairs to a variety of substrates where service temperature exceeds 200º F (93º C). It is easy to mix and apply, cures in 15-20 minutes ..
Cure Time	10.0 - 20.0 min	0.167 - 0.333 hour	Time to Handling Strength
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Cure Time	5.00 - 20.0 min	0.0833 - 0.333 hour
Resinlab® UR1049 MDI Based Rigid Polyurethane Foam System Resinlab™ UR 1049 is a, two component, water blown, 4 lb per cubic foot, MDI based rigid polyurethane foam system. It is designed to cure completely at room temperature. Being of a closed cell stru..