3M Scotch-Weld™ DP810 Black Structural Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ DP810 Black Structural Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel strength along with good impact resistance and durability. They can quickly bond to most metals, ceramics, rubbers, plastics and wood with minimal surface preparation.Information provided by 3M
Physical Properties Metric English Comments
Viscosity 17000 - 21000 cP
17000 - 21000 cP
Accelerator
18000 - 22000 cP
18000 - 22000 cP
Base
20000 cP
20000 cP
Mechanical Properties Metric English Comments
Shear Strength 0.207 MPa
30.0 psi
Overlap at 10 minutes after bonding
0.345 MPa
50.0 psi
Overlap, Acetone for 14 days, Cohesive Failure
0.517 MPa
75.0 psi
Overlap, MEK for 14 days, Cohesive Failure
3.45 MPa
500 psi
Overlap, Polycarbonate, Adhesive/Cohesive Failure
3.79 MPa
550 psi
Overlap, Acrylic, Substrate Failure
4.83 MPa
700 psi
Overlap, ABS, Adhesive/Cohesive Failure
6.89 MPa
1000 psi
Overlap, PVC, Substrate Failure
7.93 MPa
1150 psi
Overlap at 20 minutes after bonding
10.3 MPa
1500 psi
Overlap, 71°C 100% RH for 14 days, Mixed Mode of AF&CF
11.4 MPa
1650 psi
Overlap, 71°C soak for 14 days, Mixed Mode of AF&CF
15.2 MPa
2200 psi
Overlap at 1 hr after bonding
17.6 MPa
2550 psi
Overlap, Gasoline for 14 days, Cohesive Failure
17.9 MPa
2600 psi
Overlap, Toluene for 14 days, Cohesive Failure
18.6 MPa
2700 psi
Overlap at 2 hrs after bonding
20.0 MPa
2900 psi
Overlap at 2 hrs after bonding
20.7 MPa
3000 psi
Overlap, Green FRP, Cohesive Failure
21.0 MPa
3050 psi
Overlap, IPA for 14 days, Cohesive Failure
22.1 MPa
3200 psi
Overlap at 2 hrs after bonding
22.4 MPa
3250 psi
Overlap, 20% Bleach for 14 days, Cohesive Failure
23.8 MPa
3450 psi
Overlap, Oily CRS, Cohesive Failure
24.1 MPa
3500 psi
Overlap, Stainless Steel, Cohesive Failure
24.5 MPa
3550 psi
Overlap at 2 hrs after bonding
24.8 MPa
3600 psi
Overlap, CRS, Cohesive Failure
25.9 MPa
3750 psi
Overlap, Abraded Aluminum, Cohesive Failure
25.9 MPa
3750 psi
Overlap, 14 days, Cohesive Failure
26.5 MPa
3850 psi
Overlap, Bare Aluminum, Cohesive Failure
26.9 MPa
3900 psi
Overlap, 50% Antifreeze for 14 days, Cohesive Failure
27.2 MPa
3950 psi
Overlap, Diesel Fuel for 14 days, Cohesive Failure
29.0 MPa
4200 psi
Overlap, Etched Aluminum, Cohesive Failure
3.45 MPa

@Temperature 82.0 °C
500 psi

@Temperature 180 °F
Overlap
8.27 MPa

@Temperature -55.0 °C
1200 psi

@Temperature -67.0 °F
Overlap
13.8 MPa

@Temperature -29.0 °C
2000 psi

@Temperature -20.2 °F
Overlap, Adhesion Failure
13.8 MPa

@Temperature 49.0 °C
2000 psi

@Temperature 120 °F
Overlap, Cohesive Failure
24.8 MPa

@Temperature 24.0 °C
3600 psi

@Temperature 75.2 °F
Overlap
Peel Strength 5.26 kN/m
30.0 pli
T-Peel
Processing Properties Metric English Comments
Cure Time 10.0 - 20.0 min
0.167 - 0.333 hour
Time to Handling Strength
480 - 1440 min
8.00 - 24.0 hour
Full cure
Descriptive Properties Value Comments
Appearance Black
Base
White
Accelerator