3M Scotch-Weld™ DP605NS Structural Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ DP605NS Structural Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Urethane Adhesives are two-part, non-sag urethane adhesives. They feature tough, flexible bonds with good adhesion to a wide variety of substrates especially wood and many properly abraded and cleaned plastics. Good adhesion can also be obtained on etched aluminum as well as primed aluminum, steel glass. For maximum bond durability under moisture conditions, priming of glass and metal substrates is required.Information provided by 3M
Physical Properties Metric English Comments
Viscosity 150000 cP
150000 cP
Mechanical Properties Metric English Comments
Hardness, Shore A 75 - 85
75 - 85
ASTM D2240
Elongation at Break 100 %
100 %
ASTM D882
Shear Strength 9.31 MPa
1350 psi
Thermal Properties Metric English Comments
CTE, linear 121 µm/m-°C
67.2 µin/in-°F
below Tg
219 µm/m-°C
122 µin/in-°F
above Tg
Glass Transition Temp, Tg 41.0 °C
106 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Dielectric Constant 3.1

@Frequency 1000 Hz
3.1

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 25.2 kV/mm
640 kV/in
ASTM D149
Dissipation Factor 0.021

@Frequency 1000 Hz
0.021

@Frequency 1000 Hz
ASTM D150
Processing Properties Metric English Comments
Cure Time 15.0 - 20.0 min
0.250 - 0.333 hour
Time to Handling Strength
2880 min
48.0 hour
Full Cure
Descriptive Properties Value Comments
Appearance Off-White