SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³	ASTM D792
	1.24 g/cc	0.0448 lb/in³	ISO 1183
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm @Time 86400 sec	0.0060 - 0.0080 in/in @Time 24.0 hour	ASTM D955
	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0079 cm/cm @Time 86400 sec	0.0079 in/in @Time 24.0 hour	ISO 294
	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ISO 527
	48.0 MPa	6960 psi	ASTM D638
Tensile Strength, Yield	55.0 MPa	7980 psi	ASTM D638
	56.0 MPa	8120 psi	ISO 527
Elongation at Break	66.3 %	66.3 %	ASTM D638
	70.7 %	70.7 %	ISO 527
Elongation at Yield	5.7 %	5.7 %	ISO 527
	5.9 %	5.9 %	ASTM D638
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
	2.20 GPa	319 ksi	1 mm/min; ISO 527
Flexural Strength	73.0 MPa	10600 psi	ISO 178
Flexural Modulus	2.06 GPa	299 ksi	ASTM D790
	2.20 GPa	319 ksi	ISO 178
Izod Impact, Notched	1.33 J/cm	2.49 ft-lb/in	ASTM D256
Izod Impact, Unnotched	24.88 J/cm	46.61 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/m²	5.23 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	174 kJ/m²	82.8 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	40.0 J	29.5 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	44.0 J	32.5 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.24	0.24	ASTM D3702 Modified
Coefficient of Friction, Static	0.070	0.070	ASTM D3702 Modified
K (wear) Factor	68.5 x 10^-8 mm³/N-M	34.0 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	75.0 µm/m-°C @Temperature -40.0 - 40.0 °C	41.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	75.6 µm/m-°C @Temperature -40.0 - 40.0 °C	42.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	72.0 µm/m-°C @Temperature -40.0 - 40.0 °C	40.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	72.0 µm/m-°C @Temperature -40.0 - 40.0 °C	40.0 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	135 °C @Thickness 3.20 mm	275 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	125 °C	257 °F	Flatw 80104 sp=64mm; ISO 75/Af
	123 °C @Thickness 3.20 mm	253 °F @Thickness 0.126 in	unannealed; ASTM D648