SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0064 cm/cm @Time 86400 sec |
0.0064 in/in @Time 24.0 hour |
ISO 294 | |
| 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0074 cm/cm @Time 86400 sec |
0.0074 in/in @Time 24.0 hour |
ISO 294 | |
| Melt Flow | 8.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 | |
| 43.0 MPa | 6240 psi | ISO 527 | |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| 51.0 MPa | 7400 psi | ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| 32.8 % | 32.8 % | ASTM D638 | |
| 38.2 % | 38.2 % | ISO 527 | |
| Elongation at Yield | 5.3 % | 5.3 % | ASTM D638 |
| 5.3 % | 5.3 % | ISO 527 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| 2.14 GPa | 310 ksi | 1 mm/min; ISO 527 | |
| 5.09 GPa | 738 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| 2.10 GPa | 305 ksi | ISO 178 | |
| 5.01 GPa | 727 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 5.12 GPa | 743 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.54 J/cm | 2.89 ft-lb/in | ASTM D256 |
| 0.690 J/cm @Temperature -30.0 °C |
1.29 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 17.67 J/cm | 33.10 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 180 kJ/m² | 85.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 34.0 J | 25.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 32.0 J | 23.6 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.37 | 0.37 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.32 | 0.32 | ASTM D3702 Modified |
| K (wear) Factor | 42.3 x 10-8 mm³/N-M | 21.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 75.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 73.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ASTM D1525 |
| 141 °C | 286 °F | Rate B/50; ISO 306 | |
| 145 °C | 293 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.700 mm |
HB @Thickness 0.0276 in |
UL 94 |
Users viewing this material also viewed the following:
- Plenco 50015 PET, Pellet, Injection Molded, White (discontinued **)
- Mallard Creek Polymers ROVENE® 4176 SBR Latex
- Iran Petrochemical (PCC) MF3313 High Density Polyethylene
- Monmouth Rubber & Plastics Durafoamâ„¢ IVN 41 NEO/PVC/NBR
- Silberline SilBerCote® 1703-20Z
- DSM Arnitel® PM381 Polyether Ester Elastomer (European Grade)
- ChevronTexaco Hydraulic Safety Fluid
- CP-Polymer-Technik Wellamid® 6000 GS 50 HWUVCP 50% Glass Sphere Filled Nylon 6, UV Stabilized Heat Stabilized, Conditioned
- Henkel SynCore 9823.1 Syntactic Film
Copyright © lookpolymers.com All Rights Reserved