HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer High Performance Alloys, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Physical Properties Metric English Comments
Density 9.22 g/cc
0.333 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 298
298
Estimated from Rockwell C
Hardness, Knoop 352
352
Estimated from Rockwell C
Hardness, Rockwell A 66.5
66.5
Estimated from Rockwell C
Hardness, Rockwell C 32
32
Hardness, Vickers 309
309
Estimated from Rockwell C
Modulus of Elasticity 189 GPa

@Thickness 12.7 mm,
Temperature 538 °C
27400 ksi

@Thickness 0.500 in,
Temperature 1000 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
196 GPa

@Thickness 12.7 mm,
Temperature 427 °C
28400 ksi

@Thickness 0.500 in,
Temperature 800 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
202 GPa

@Thickness 12.7 mm,
Temperature 316 °C
29300 ksi

@Thickness 0.500 in,
Temperature 600 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
217 GPa

@Thickness 12.7 mm,
Temperature 21.1 °C
31500 ksi

@Thickness 0.500 in,
Temperature 70.0 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
Thermal Properties Metric English Comments
CTE, linear 10.3 µm/m-°C

@Temperature 20.0 - 93.0 °C
5.72 µin/in-°F

@Temperature 68.0 - 199 °F
10.8 µm/m-°C

@Temperature 20.0 - 204 °C
6.00 µin/in-°F

@Temperature 68.0 - 399 °F
11.2 µm/m-°C

@Temperature 20.0 - 316 °C
6.22 µin/in-°F

@Temperature 68.0 - 601 °F
11.5 µm/m-°C

@Temperature 20.0 - 427 °C
6.39 µin/in-°F

@Temperature 68.0 - 801 °F
11.7 µm/m-°C

@Temperature 20.0 - 538 °C
6.50 µin/in-°F

@Temperature 68.0 - 1000 °F
Specific Heat Capacity 0.373 J/g-°C

@Temperature 0.000 °C
0.0891 BTU/lb-°F

@Temperature 32.0 °F
0.389 J/g-°C

@Temperature 100 °C
0.0930 BTU/lb-°F

@Temperature 212 °F
0.406 J/g-°C

@Temperature 200 °C
0.0970 BTU/lb-°F

@Temperature 392 °F
0.423 J/g-°C

@Temperature 300 °C
0.101 BTU/lb-°F

@Temperature 572 °F
0.431 J/g-°C

@Temperature 400 °C
0.103 BTU/lb-°F

@Temperature 752 °F
0.444 J/g-°C

@Temperature 500 °C
0.106 BTU/lb-°F

@Temperature 932 °F
0.456 J/g-°C

@Temperature 600 °C
0.109 BTU/lb-°F

@Temperature 1110 °F
Thermal Conductivity 11.1 W/m-K

@Temperature 0.000 °C
77.0 BTU-in/hr-ft²-°F

@Temperature 32.0 °F
12.2 W/m-K

@Temperature 100 °C
84.7 BTU-in/hr-ft²-°F

@Temperature 212 °F
13.4 W/m-K

@Temperature 200 °C
93.0 BTU-in/hr-ft²-°F

@Temperature 392 °F
14.6 W/m-K

@Temperature 300 °C
101 BTU-in/hr-ft²-°F

@Temperature 572 °F
16.0 W/m-K

@Temperature 400 °C
111 BTU-in/hr-ft²-°F

@Temperature 752 °F
17.3 W/m-K

@Temperature 500 °C
120 BTU-in/hr-ft²-°F

@Temperature 932 °F
18.7 W/m-K

@Temperature 600 °C
130 BTU-in/hr-ft²-°F

@Temperature 1110 °F
Component Elements Properties Metric English Comments
Carbon, C 0.010 %
0.010 %
Chromium, Cr 1.0 %
1.0 %
Cobalt, Co <= 1.0 %
<= 1.0 %
Iron, Fe <= 2.0 %
<= 2.0 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Molybdenum, Mo 28 %
28 %
Nickel, Ni 69 %
69 %
Silicon, Si <= 0.10 %
<= 0.10 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000137 ohm-cm

@Temperature 0.000 °C
0.000137 ohm-cm

@Temperature 32.0 °F
0.000138 ohm-cm

@Temperature 100 °C
0.000138 ohm-cm

@Temperature 212 °F
0.000138 ohm-cm

@Temperature 200 °C
0.000138 ohm-cm

@Temperature 392 °F
0.000139 ohm-cm

@Temperature 300 °C
0.000139 ohm-cm

@Temperature 572 °F
0.000139 ohm-cm

@Temperature 400 °C
0.000139 ohm-cm

@Temperature 752 °F
0.000141 ohm-cm

@Temperature 500 °C
0.000141 ohm-cm

@Temperature 932 °F
0.000146 ohm-cm

@Temperature 600 °C
0.000146 ohm-cm

@Temperature 1110 °F