Schmolz + Bickenbach Cryodur® 2363 (A-2) Cold Work Die Steel

Category Metal , Ferrous Metal , Tool Steel , Cold Work Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name Cryodur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach Cryodur® 2363 (A-2) Cold Work Die Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Cryodur® 2363 is a cold-work steel developed for an excellent combination of wear resistance and toughness and Supplied in the annealed conditionCharacteristics: Good wear resistance; Good toughness; High compressive strength; and Good stability after heat treatmentApplications: Forming Rolls, Cold stamping tools, Inserts for processing abrasive plastics, Coining die, Guide rails, and Trim dieStress Relieving (Heat Treatment): 1200°F-1290°F; Cooling: Hold time 2 hours. slowly cool to 930°F, then air coolHardening (Heat Treatment): 1700°F-1780°F Hold at temperature for 30 minutes; Cooling: Furnace quench to 350°F, air cool to 120°F, immediately temper; Hardness:
Physical Properties Metric English Comments
Density 7.72 g/cc
0.279 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 52

@Treatment Temp. 600.0 °C,
Time 7200 sec
52

@Treatment Temp. 1112 °F,
Time 2.00 hour
57

@Treatment Temp. 400 °C,
Time 7200 sec
57

@Treatment Temp. 752 °F,
Time 2.00 hour
59

@Treatment Temp. 300 °C,
Time 7200 sec
59

@Treatment Temp. 572 °F,
Time 2.00 hour
59

@Treatment Temp. 500 °C,
Time 7200 sec
59

@Treatment Temp. 932 °F,
Time 2.00 hour
62

@Treatment Temp. 200 °C,
Time 7200 sec
62

@Treatment Temp. 392 °F,
Time 2.00 hour
63

@Treatment Temp. 100 °C,
Time 7200 sec
63

@Treatment Temp. 212 °F,
Time 2.00 hour
Compressive Strength 1790 MPa
260000 psi
55 HRC
2140 MPa
310000 psi
60 HRC
2210 MPa
320000 psi
62 HRC
Thermal Properties Metric English Comments
CTE, linear 11.7 µm/m-°C

@Temperature 21.1 - 204 °C
6.50 µin/in-°F

@Temperature 70.0 - 400 °F
Thermal Conductivity 15.9 W/m-K

@Temperature 20.0 °C
110 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
26.7 W/m-K

@Temperature 343 °C
185 BTU-in/hr-ft²-°F

@Temperature 650 °F
29.1 W/m-K

@Temperature 704 °C
202 BTU-in/hr-ft²-°F

@Temperature 1300 °F
Component Elements Properties Metric English Comments
Carbon, C 1.0 %
1.0 %
Chromium, Cr 5.0 %
5.0 %
Iron, Fe 92.05 %
92.05 %
Manganese, Mn 0.50 %
0.50 %
Molybdenum, Mo 0.95 %
0.95 %
Silicon, Si 0.30 %
0.30 %
Vanadium, V 0.20 %
0.20 %
Processing Properties Metric English Comments
Annealing Temperature 801.7 - 849 °C
1475 - 1560 °F
Soft; Cooling: Furnace 20°F/hour to 1200°F/ Then air cool; < 231 HB