Polymer Property : Maximum Service Temperature, Air = 208 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	97.8 °C	208 °F	Heat Distortion, Annealed; ASTM D648
Total 819E Polystyrene (discontinued **) Polystyrene 819E is a high impact polystyrene extrusion grade with very high stiffness and thermal properties.It makes an excellent gloss/cut resistant layer for foam applications or general thermof..
Maximum Service Temperature, Air	97.8 °C	208 °F	Heat Distortion, Annealed; ASTM D648
Total 965E Polystyrene (discontinued **) Polystyrene 965E is a high-impact polystyrene. The extruder will see that 965E produces sheet with a dull matte finish and superior wetting tension to meet the printers needs.965E is specially desig..
Maximum Service Temperature, Air	98.0 °C	208 °F	Continuous; FRISETTA Test Method
Nilit RECONYL B KV30 Recycled nylon 6 for injection molding, 30% glass ball reinforced Recycled nylon 6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Maximum Service Temperature, Air	98.0 Â°C	208 Â°F	Heat Distortion Temp
Lucky IH-830 Acrylic, Injection Grade Similar to grade EH-910, but with higher flow for injection molding. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent..
Maximum Service Temperature, Air	98.0 Â°C	208 Â°F	Deflection Temp; Load not reported; ASTM D648
Lucky IH-830 Acrylic, Injection Grade Similar to grade EH-910, but with higher flow for injection molding. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent..
Maximum Service Temperature, Air	98.0 Â°C	208 Â°F	Deflection Temp; Load not reported; ASTM D648
Lucky CH-910 Acrylic, Coextrusion Grade Coextrusion grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.
Maximum Service Temperature, Air	98.0 Â°C	208 Â°F	Heat Distortion Temp
Lucky CH-910 Acrylic, Coextrusion Grade Coextrusion grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.
Maximum Service Temperature, Air	98.0 - 300 °C	208 - 572 °F	Average value: 227 °C Grade Count:6
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value..
Maximum Service Temperature, Air	98.0 °C	208 °F	Deflection Temp; Load not specified; ASTM D648
Fibre Glast 1110 CC Vinyl Ester Resin (Casting Properties) (discontinued **) #1110 is a low viscosity, corrosion resistant vinyl ester resin. It is formulated for maximum corrosion resistance to most fuels, vapors, and both acidic and basic chemicals. It is also heat resista..
Maximum Service Temperature, Air	98.0 °C	208 °F	Heat Distortion Temp
Lucky EH-910 Acrylic, Extrusion Grade Highest heat and stress cracking resistance of Lucky PMMA grades. Recommended for extrusion of sheets, pipes, and profiles. Can also be used for injection molding of small parts. May be UV stabil..
Maximum Service Temperature, Air	98.0 °C	208 °F	Deflection Temp; Load not reported; ASTM D648
Lucky EH-910 Acrylic, Extrusion Grade Highest heat and stress cracking resistance of Lucky PMMA grades. Recommended for extrusion of sheets, pipes, and profiles. Can also be used for injection molding of small parts. May be UV stabil..