Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a broad temperature range. It also displays low moisture absorption, excellent chemical resistance and excellent electrical properties.Features: Fast Molding Cycle; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Flow; High Stiffness; High Strength; Hot Water Moldability; Low Moisture Absorption; LubricatedUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bobbins; Camera Applications; Cell Phones; Connectors; Electrical/Electronic Applications; General Purpose; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Water Absorption 0.26 %

@Time 86400 sec
0.26 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 180 MPa
26100 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-2
Flexural Strength 255 MPa
37000 psi
ISO 178
Flexural Modulus 11.0 GPa
1600 ksi
ISO 178
Izod Impact, Notched (ISO) 8.40 kJ/m²
4.00 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
Type 1; ISO 180
Charpy Impact, Notched 0.820 J/cm²
3.90 ft-lb/in²
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C

@Temperature 150 - 250 °C
7.78 µin/in-°F

@Temperature 302 - 482 °F
2
20.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
11.1 µin/in-°F

@Temperature 32.0 - 194 °F
2
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
35.0 µin/in-°F

@Temperature 32.0 - 194 °F
TMA; ASTM E831
150 µm/m-°C

@Temperature 100 - 250 °C
83.3 µin/in-°F

@Temperature 212 - 482 °F
TMA; ASTM E831
Melting Point 327 °C
621 °F
DSC; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 310 °C
590 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Glow Wire Test 800 °C
1470 °F
Glow Wire Ignition Temperature; IEC 60695-2-13
800 °C
1470 °F
Glow Wire Flammability Index, IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
ASTM D150
3.9

@Frequency 60.0 Hz
3.9

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Dissipation Factor 0.0060

@Frequency 60.0 Hz
0.0060

@Frequency 60.0 Hz
ASTM D150
0.016

@Frequency 1.00e+6 Hz
0.016

@Frequency 1.00e+6 Hz
ASTM D150
High Voltage Arc Resistance to Ignition (HVAR) >= 300 sec
>= 300 sec
UL 746
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 318 - 324 °C
604 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 329 - 343 °C
624 - 649 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Additive Lubricant; Mold Release
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Natural
Form Pellets
Processing Technique Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant