E-Polymers TEKAMID® TA250G60 60% Glass Fiber Reinforced, High Modulus PA66 Resin

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® TA250G60 60% Glass Fiber Reinforced, High Modulus PA66 Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified, Super tough productsInformation Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D792
Water Absorption 0.40 %

@Time 86400 sec
0.40 %

@Time 24.0 hour
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength 216 MPa
31300 psi
ASTM D638
Elongation at Break 1.8 %
1.8 %
ASTM D638
Flexural Strength 324 MPa
47000 psi
ASTM D790
Flexural Modulus 16.7 GPa
2420 ksi
ASTM D790
Izod Impact, Notched 1.57 J/cm
2.94 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 252 °C
486 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 90.0 - 120 °C
194 - 248 °F