 POLYMER SEARCH

Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R543H BK02 is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in black, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep, higher impact and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including many aliphatic, and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils. Vydyne R543H BK02 resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts. Vydyne R543H BK02 is formulated to minimize the oxidative and thermal degradation of the PA66 polymer when exposed to elevated temperatures for extended periods of time. Vydyne R543H BK02 provides improved retention of physical properties under exposure to long term heat. The continuous operating use temperature is 275°F, with short-term peak temperatures as high as 475°F. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by WeightAdditive:Heat StabilizerLubricant Features:Gasoline ResistanceGood Chemical ResistanceGood Creep ResistanceGood Dimensional StabilityGood Impact ResistanceGood Mold ReleaseGrease ResistantHeat StabilizedHigh Flow High RigidityHigh StrengthHigh Tensile Strength LubricatedOil ResistantSolvent Resistant Uses: Automotive Under the HoodGearsHousingsLawn and Garden EquipmentPower/Other Tools Appearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 0.60 %

@Time 86400 sec
0.60 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Diameter 2.00 mm
0.0040 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Diameter 2.00 mm
0.0090 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 225 MPa
32600 psi
ISO 527-2
Elongation at Break 3.0 %
3.0 %
ISO 527-2
Tensile Modulus 14.8 GPa
2150 ksi
ISO 527-2
Flexural Strength 340 MPa
49300 psi
ISO 178
Flexural Modulus 12.5 GPa
1810 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 180
13.0 kJ/m²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 8.70 J/cm²

@Temperature -30.0 °C
41.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
9.20 J/cm²

@Temperature 23.0 °C
43.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.40 J/cm²

@Temperature 23.0 °C
6.66 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 1.60 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
0.889 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 252 °C
486 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 140 °C

@Thickness 0.750 mm
284 °F

@Thickness 0.0295 in
UL 746
140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
UL 746
140 °C

@Thickness 3.00 mm
284 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 130 °C

@Thickness 0.750 mm
266 °F

@Thickness 0.0295 in
UL 746
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 140 °C

@Thickness 0.750 mm
284 °F

@Thickness 0.0295 in
UL 746
140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
UL 746
140 °C

@Thickness 3.00 mm
284 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Glow Wire Test 675 °C

@Thickness 0.750 mm
1250 °F

@Thickness 0.0295 in
Flammability Index; IEC 60695-2-12
675 °C

@Thickness 1.50 mm
1250 °F

@Thickness 0.0591 in
Flammability Index; IEC 60695-2-12
700 °C

@Thickness 0.750 mm
1290 °F

@Thickness 0.0295 in
Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
1290 °F

@Thickness 0.0591 in
Ignition Temperature; IEC 60695-2-13
750 °C

@Thickness 3.00 mm
1380 °F

@Thickness 0.118 in
Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm

@Thickness 0.750 mm
1.00e+12 ohm-cm

@Thickness 0.0295 in
IEC 60093
Dielectric Strength 20.0 kV/mm

@Thickness 1.00 mm
508 kV/in

@Thickness 0.0394 in
IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
120 - 179 sec

@Thickness 0.118 in
ASTM D495
Comparative Tracking Index 400 - 499 V

@Thickness 3.00 mm
400 - 499 V

@Thickness 0.118 in
IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.750 mm
7.0 - 14 sec

@Thickness 0.0295 in
UL 746
7.0 - 14 sec

@Thickness 3.00 mm
7.0 - 14 sec

@Thickness 0.118 in
UL 746
15 - 29 sec

@Thickness 1.50 mm
15 - 29 sec

@Thickness 0.0591 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
>= 120 arcs

@Thickness 0.0295 in
UL 746
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 10.1 - 25.4 mm/min
0.398 - 1.00 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 310 °C
536 - 590 °F
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Front Barrel Temperature 280 - 310 °C
536 - 590 °F
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Melt Temperature 285 - 305 °C
545 - 581 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %