- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 48.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 48.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C @Thickness 4.00 mm |
118 °F @Thickness 0.157 in |
after annealing 150°C 16 hr; ASTM D648 |
| Solvay Specialty Polymers Solef® 32008 PVDF Copolymer
(Unverified Data**) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 - 99.0 °C | 118 - 210 °F | Average value: 74.1 °C Grade Count:88 |
| Overview of materials for High Density Polyethylene (HDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Blow Molding Grade". Each property range of values reported is minimum.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| LyondellBasell Petrothene® GA818073 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 818-073 offers the high environmental stress crack resistance characteristics of linear low density polyethylene with the processing properties needed for blowmolding and e.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| LyondellBasell Purell® PE3220D Low Density Polyethylene, Injection Molding, Blow Fill & Seal, Extrusion Blow Molding Purell PE 3220 D is a low density polyethylene with high rigidity and good chemical resistance. It is delivered in pellet form. Target markets are packaging of pharmaceuticals in the small blow mold.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| DuPont™ Surlyn® 9650 Ionomer Resin, Zinc Surlyn® 9650 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Hytrel® DYM250S BK472 TPC-ET+PBT
(Unverified Data**) Medium Modulus Polyester Elastomer with Excellent Impact Resistance Developed for Air Bag Door ApplicationsHytrel DYM250S BK472 is a medium modulus resin suited for injection molding of Air Bag Depl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM D648 |
| 3D Systems Accura® ClearVue™ Free (SL 7870) Stereolithography Plastic High clarity plastic for a multitude of applicationsFeaturesClear and transparentRigid and toughGreat for headlamps, bottles and transparent assembliesExcellent humidity/moisture resistanceAll infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM-D648 |
| Braskem PCD 0440 HECO Polypropylene Heterophasic Copolymer PCD 0440 is a medium melt flow rate heterophasic copolymer with high impact strength. This resin is designed for steel pipe coating (SPC) and injection molding. Its applications include: automotive.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 °C | 118 °F | ASTM-D648 |
| Braskem Symbios 4102 Polypropylene Terpolymer Braskem Symbios 4102 is a medium melt flow rate terpolymer with a heat seal temperature below 120ºC on its treated face. It is designed for use as a heat sealing layer on bioriented films (BOPP) an.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 - 51.0 °C | 118 - 124 °F | Average value: 50.0 °C Grade Count:3 |
| Overview of materials for Linear Low Density Polyethylene (LLDPE), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Extrusion Grade". Each property range of values reported is min.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 48.0 - 129 °C | 118 - 264 °F | Average value: 95.3 °C Grade Count:109 |
| Overview of materials for Polypropylene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Film Grade". Each property range of values reported is minimum and maximum values of appr.. |
|||