Solvay Specialty Polymers Solef® 32008 PVDF Copolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Solef® 32008 PVDF Copolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystalline thermoplastic which is obtained by polymerizing vinylidene fluoride. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, high purity, resistance to UV and nuclear radiation, excellent intrinsic fire resistance, resistance to weathering, low permeability to most gases and liquids, and easily melt-processed by standard methods of molding and extrusion.Tensile properties are achieved with varying methods of sample fabrication. Information provided by Solvay Solexis, Inc.
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
ISO 62 (method 1)
Linear Mold Shrinkage 0.020 - 0.030 cm/cm
0.020 - 0.030 in/in
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
15 g/10 min

@Load 5.00 kg,
Temperature 230 °C
15 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 47

@Thickness 2.00 mm
47

@Thickness 0.0787 in
ASTM D2240
Tensile Strength, Ultimate 14.0 - 30.0 MPa
2030 - 4350 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 14.0 - 35.0 MPa
2030 - 5080 psi
50 mm/min; ASTM D638
Elongation at Break 350 - 600 %
350 - 600 %
50 mm/min; ASTM D638
Elongation at Yield 10 - 12 %
10 - 12 %
50 mm/min; ASTM D638
Modulus of Elasticity 0.200 GPa
29.0 ksi
1 mm/min; ASTM D638
Flexural Yield Strength 8.00 MPa
1160 psi
2 mm/min; ASTM D790
Flexural Modulus 0.200 GPa
29.0 ksi
2 mm/min; ASTM D790
Izod Impact, Notched NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
Notched V 10 mm; ASTM D256
Coefficient of Friction 0.20 - 0.30
0.20 - 0.30
ASTM D1894
Coefficient of Friction, Static 0.20 - 0.40
0.20 - 0.40
ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0 - 15
5.0 - 15
CS10 / 1 kg
Thermal Properties Metric English Comments
Heat of Fusion 17.0 J/g
7.31 BTU/lb
80°C to end of melting
19.0 J/g
8.17 BTU/lb
Crystallization Heat
CTE, linear 130 - 150 µm/m-°C

@Temperature 20.0 °C
72.2 - 83.3 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 1.20 J/g-°C
0.287 BTU/lb-°F
1.60 J/g-°C

@Temperature 100 °C
0.382 BTU/lb-°F

@Temperature 212 °F
Thermal Conductivity 0.180 W/m-K
1.25 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 168 °C
334 °F
Crystallinity by DSC; ASTM D 3418
Crystallization Temperature 128 °C
262 °F
Deflection Temperature at 0.46 MPa (66 psi) 48.0 °C

@Thickness 4.00 mm
118 °F

@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Vicat Softening Point 75.0 °C

@Load 1.00 kg,
Thickness 4.00 mm
167 °F

@Load 2.20 lb,
Thickness 0.157 in
ISO 306
Brittleness Temperature -53.0 °C
-63.4 °F
ASTM D746A
Glass Transition Temp, Tg -28.0 °C
-18.4 °F
DMTA
Decomposition Temperature 320 - 340 °C
608 - 644 °F
Thermal Stability via TGA : beginning - and at 1% weight loss in air
Oxygen Index 50 - 65 %

@Thickness 3.00 mm
50 - 65 %

@Thickness 0.118 in
sheet; ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483
Dielectric Constant 7.0

@Frequency 1e+6 Hz
7.0

@Frequency 1e+6 Hz
ASTM D150