SABIC Innovative Plastics LNP FARADEX ES003E PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP FARADEX ES003E PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* FARADEX* ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ASTM D792
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
Moisture Absorption 0.190 %
0.190 %
50% RH, 24 hrs; ASTM D570
0.270 %
0.270 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 98.0 MPa
14200 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 99.0 MPa
14400 psi
5 mm/min; ISO 527
105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 4.3 %
4.3 %
5 mm/min; ISO 527
5.0 %
5.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
5 mm/min; ISO 527
4.8 %
4.8 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.34 GPa
629 ksi
1 mm/min; ISO 527
4.66 GPa
676 ksi
50 mm/min; ASTM D638
Flexural Strength 155 MPa
22500 psi
ISO 178
Flexural Modulus 4.31 GPa
625 ksi
2 mm/min; ISO 178
4.59 GPa
666 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.340 J/cm
0.637 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.85 J/cm
9.09 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 22.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 44.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 24.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 194 °C
381 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
190 °C

@Thickness 3.20 mm
 374 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
180 °C

@Thickness 3.20 mm
 356 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 2.0 - 4.0 ohm
2.0 - 4.0 ohm
ASTM D257
Shielding Effectiveness 60 dB

@Thickness 2.50 mm
 60 dB

@Thickness 0.0984 in
 SABIC Method