Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Polymer Resources PC-GP1-[color]-LF Polycarbonate, General Purpose, Food Contact Polycarbonate, General Purpose, Low FlowFeatures: • Food Contact AcceptableProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Polymer Resources PPX/NY GP1 PPO/Nylon 66 Alloy Polyphenylene Oxide/Nylon 66 Alloy , General PurposeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Hylex® P1007L Polycarbonate Information provided by Ravago |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Hylex® P1307L Polycarbonate Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Fiberfil® J-61/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 3.17 mm |
285 °F @Thickness 0.125 in |
un-annealed; ASTM D648 |
MRC Polymers NAXELLâ„¢ PC23M-10G General Purpose Polycarbonate, 10% Glass Fiber Filled, Low Viscosity Can be impact modifiedInternal and external lubricant can be addedBlack onlyInformation provided by MRC Polymers Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® POM CO GC25 25% Glass Bead Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 25% Filler by WeightFeatures: CopolymerInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Westlake Plastics Norylux™ Modified Polyphenylene Oxide 30% glass filled Norylux modified PPO is a strong, engineering plastic with outstanding mechanical, thermal, and electric properties. Low moisture absorption and low thermal expansion make Norylux one of the most d.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
Entec Hylex® P1017FR Polycarbonate Information provided by Ravago. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
Entec Hylex® P1317FR Polycarbonate Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Adell DR-12 10% Glass Reinforced Polycarbonate |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Asahi Kasei Thermylene® P6-15FG-1734 15% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 - 207 °C | 285 - 405 °F | Average value: 164 °C Grade Count:25 |
Overview of materials for Acetal Copolymer, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Glass Bead Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
Polymer Resources PPX/NY GP1 Modified PPO, General Purpose PPX/Nylon 6,6 Alloy
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |