Polymer Resources PPX/NY GP1 Modified PPO, General Purpose PPX/Nylon 6,6 Alloy  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX/NY GP1 Modified PPO, General Purpose PPX/Nylon 6,6 Alloy  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0090 - 0.012 cm/cm
0.0090 - 0.012 in/in
ASTM D955
Melt Flow 20 - 40 g/10 min
20 - 40 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D638
Tensile Strength, Yield 57.9 MPa
8400 psi
ASTM D638
Flexural Strength 8.62 MPa
1250 psi
ASTM D790
Flexural Modulus 2.07 GPa
300 ksi
ASTM D790
Izod Impact, Notched 2.14 J/cm
4.00 ft-lb/in
ASTM D256
Gardner Impact >= 28.2 J
>= 20.8 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 141 °C
285 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 299 °C
500 - 570 °F
Middle Barrel Temperature 266 - 299 °C
510 - 570 °F
Front Barrel Temperature 271 - 299 °C
520 - 570 °F
Melt Temperature 277 - 299 °C
530 - 570 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 93.3 - 107 °C
200 - 225 °F
Dry Time 3 - 5 hour
3 - 5 hour