- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 223 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 223 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 - 245 °C | 433 - 473 °F | Average value: 236 °C Grade Count:4 |
| Overview of materials for Polyethylene Terephthalate (PET), Recycled, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Recycled, Glass/Mineral Reinforced". Each property range of values rep.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data**) Sorona® 3015GV NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness and sur.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data** Sorona® FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) formulated to be food c.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® NL-43GF/000 Nylon 6/12, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/-2 |
| Lanxess Pocan® DP 7244 000000 PBT, 30% Glass Fiber PBT, 30% glass fibers, injection molding, flame retardant |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 LNP* LUBRICOMP* RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® SHF4340 PBT (Europe-Africa-Middle East) 20% GF Super High Flow PBT |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES LNP* Thermocomp* JF004LZ is a compound based on PES containing 20% Glass Fiber. Added features include: Extrusion Grade, Low Extractible. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP JF004RXP PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004RXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp WC006 Polyester, TP LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP WC006 Polyester, TP (Asia Pacific) LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP WCL36 PBT LNP* LUBRICOMP* WCL36 is a compound based on PBT resin containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C @Thickness 6.40 mm |
433 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 430 PBT (Asia Pacific) 33 % glass reinforced, impact modified. Connectors, etc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP QC008 PA6.10 LNP* THERMOCOMP* QC008 is a compound based on Nylon 6/10 containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Cheng Yu Plastic T888G1 PBT, 10% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| PolyOne Edgetek® NL-45GF/000 Nylon 6/12 - 45% Glass Fiber
(discontinued **) Data provided by PolyOne. |
|||