DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sorona® 3015GV NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness and surface appearance in a broad range of conditions.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.080 %

@Temperature 23.0 °C
 0.080 %

@Temperature 73.4 °F
 Immersion 24h; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 2.00 mm
 0.0020 in/in

@Thickness 0.0787 in
 Mold 80°C; ISO 294-4
0.0030 cm/cm

@Thickness 3.00 mm
 0.0030 in/in

@Thickness 0.118 in
 Mold 80°C; ISO 294-4
0.0040 cm/cm

@Thickness 4.00 mm
 0.0040 in/in

@Thickness 0.157 in
 Mold 80°C; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 2.00 mm
 0.0070 in/in

@Thickness 0.0787 in
 Mold 80°C; ISO 294-4
0.0070 cm/cm

@Thickness 3.00 mm
 0.0070 in/in

@Thickness 0.118 in
 Mold 80°C; ISO 294-4
0.010 cm/cm

@Thickness 4.00 mm
 0.010 in/in

@Thickness 0.157 in
 Mold 80°C; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa

@Temperature 23.0 °C
 18100 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 3.0 %

@Temperature 23.0 °C
 3.0 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 6.50 GPa

@Temperature 23.0 °C
 943 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 190 MPa

@Temperature 23.0 °C
 27600 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 5.80 GPa

@Temperature 23.0 °C
 841 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched 2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²

@Temperature 23.0 °C
 2.62 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 160 °C
 278 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 74.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 41.1 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
89.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 49.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
132 µm/m-°C

@Temperature 55.0 - 160 °C
 73.3 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
Melting Point 227 °C
441 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 223 °C
433 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 UL94
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL94
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 UL94
Oxygen Index 19 %
19 %
ISO 4589-1/-2
Glow Wire Test 650 °C

@Thickness 1.50 mm
 1200 °F

@Thickness 0.0591 in
 IEC 60695-2-12
675 °C

@Thickness 0.850 mm
 1250 °F

@Thickness 0.0335 in
 IEC 60695-2-12
675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Ignition; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 IEC 60695-2-12
700 °C

@Thickness 0.850 mm
 1290 °F

@Thickness 0.0335 in
 Ignition; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
 1340 °F

@Thickness 0.118 in
 Ignition; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+16 ohm-cm

@Temperature 23.0 °C
 2.00e+16 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Surface Resistance 1.00e+14 ohm

@Temperature 23.0 °C
 1.00e+14 ohm

@Temperature 73.4 °F
 IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.7

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 IEC 60250
3.9

@Frequency 100 Hz,
Temperature 23.0 °C
 3.9

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
3.9

@Frequency 1000 Hz,
Temperature 23.0 °C
 3.9

@Frequency 1000 Hz,
Temperature 73.4 °F
 IEC 60250
Dielectric Strength 27.0 kV/mm

@Thickness 2.00 mm,
Temperature 23.0 °C
 686 kV/in

@Thickness 0.0787 in,
Temperature 73.4 °F
 IEC 60243-1
27.0 kV/mm

@Thickness 2.00 mm,
Temperature 90.0 °C
 686 kV/in

@Thickness 0.0787 in,
Temperature 194 °F
 IEC 60243-1
36.0 kV/mm

@Thickness 1.00 mm,
Temperature 23.0 °C
 914 kV/in

@Thickness 0.0394 in,
Temperature 73.4 °F
 IEC 60243-1
36.0 kV/mm

@Thickness 1.00 mm,
Temperature 90.0 °C
 914 kV/in

@Thickness 0.0394 in,
Temperature 194 °F
 IEC 60243-1
Dissipation Factor 0.0015

@Frequency 100 Hz,
Temperature 23.0 °C
 0.0015

@Frequency 100 Hz,
Temperature 73.4 °F
 IEC 60250
0.0027

@Frequency 1000 Hz,
Temperature 23.0 °C
 0.0027

@Frequency 1000 Hz,
Temperature 73.4 °F
 IEC 60250
Comparative Tracking Index 250 V

@Temperature 23.0 °C
 250 V

@Temperature 73.4 °F
 IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Optimum
250 - 270 °C
482 - 518 °F
Mold Temperature 80.0 - 110 °C
176 - 230 °F
100 °C
212 °F
optimum
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Appearance Natural Color
Forms Pellets
Generic Polytrimethylene Terephthalate (PTT)
Material Status Current
Part Marking Code >PTT-GF15<
ISO 11469
Processing Method Injection Molding
Product Category Glass Reinforced Resins
Renewably Sourced Resins
Region Available - Global Yes
Resin Identification PTT-GF15
ISO 1043
RoHS Compliance Contact Manufacturer