DuPont Performance Polymers Delrin® 500P BK602 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500P BK602 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium Viscosity Acetal Homopolymer with Improved ProcessingDelrin 500P BK602 is a general purpose medium viscosity black acetal homopolymer resin for injection molding. Delrin 500P has improved processing thermal stability compared to Delrin 500.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 16.5 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 2390 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
33.4 MPa

@Strain 0.900 %,
Temperature -40.0 °C
 4840 psi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
47.5 MPa

@Strain 2.30 %,
Temperature 23.0 °C
 6890 psi

@Strain 2.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
59.6 MPa

@Strain 4.00 %,
Temperature 23.0 °C
 8640 psi

@Strain 4.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
64.6 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 9370 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
80.4 MPa

@Strain 3.70 %,
Temperature -40.0 °C
 11700 psi

@Strain 3.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
90.2 MPa

@Strain 6.00 %,
Temperature -40.0 °C
 13100 psi

@Strain 6.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
93.5 MPa

@Strain 9.00 %,
Temperature -40.0 °C
 13600 psi

@Strain 9.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 71.0 MPa
10300 psi
ISO 527-1/-2
Elongation at Break 25 %
25 %
Nominal; ISO 527-1/-2
Elongation at Yield 14 %
14 %
ISO 527-1/-2
Tensile Modulus 3.10 GPa
450 ksi
ISO 527-1/-2
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Secant Modulus 0.314 GPa

@Strain 8.50 %,
Temperature 100 °C
 45.6 ksi

@Strain 8.50 %,
Temperature 212 °F
 ISO 11403-1 -2
0.494 GPa

@Strain 5.00 %,
Temperature 100 °C
 71.6 ksi

@Strain 5.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.500 GPa

@Strain 7.00 %,
Temperature 80.0 °C
 72.5 ksi

@Strain 7.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.614 GPa

@Strain 3.50 %,
Temperature 100 °C
 89.1 ksi

@Strain 3.50 %,
Temperature 212 °F
 ISO 11403-1 -2
0.636 GPa

@Strain 15.0 %,
Temperature -40.0 °C
 92.2 ksi

@Strain 15.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
0.7575 GPa

@Strain 4.00 %,
Temperature 80.0 °C
 109.9 ksi

@Strain 4.00 %,
Temperature 176 °F
 ISO 11403-1 -2
0.812 GPa

@Strain 1.70 %,
Temperature 100 °C
 118 ksi

@Strain 1.70 %,
Temperature 212 °F
 ISO 11403-1 -2
0.83125 GPa

@Strain 8.00 %,
Temperature 23.0 °C
 120.56 ksi

@Strain 8.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.850 GPa

@Strain 0.400 %,
Temperature 100 °C
 123 ksi

@Strain 0.400 %,
Temperature 212 °F
 ISO 11403-1 -2
0.857 GPa

@Strain 11.0 %,
Temperature -40.0 °C
 124 ksi

@Strain 11.0 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.045 GPa

@Strain 2.00 %,
Temperature 80.0 °C
 151.6 ksi

@Strain 2.00 %,
Temperature 176 °F
 ISO 11403-1 -2
1.31 GPa

@Strain 7.00 %,
Temperature -40.0 °C
 191 ksi

@Strain 7.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.33 GPa

@Strain 4.60 %,
Temperature 23.0 °C
 194 ksi

@Strain 4.60 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.42 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 206 ksi

@Strain 0.500 %,
Temperature 176 °F
 ISO 11403-1 -2
2.07 GPa

@Strain 2.30 %,
Temperature 23.0 °C
 300 ksi

@Strain 2.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.17 GPa

@Strain 3.70 %,
Temperature -40.0 °C
 315 ksi

@Strain 3.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
3.30 GPa

@Strain 0.500 %,
Temperature 23.0 °C
 479 ksi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.71 GPa

@Strain 0.900 %,
Temperature -40.0 °C
 538 ksi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
8.00 kJ/m²

@Temperature -40.0 °C
 3.81 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Charpy Impact Unnotched 18.0 J/cm²
85.7 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 115 µm/m-°C
63.9 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 162 °C
324 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 96.0 °C
205 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Lubricants
Release agent
Delivery Form Pellets
Part Marking Code >POM<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM
ISO 1043
UL recognition UL
Users viewing this material also viewed the following: