PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer)

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer PolyOne Corporation
Trade Name Maxxam™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer).pdf
  Online Service   lookpolymers   27660005
Material Notes:
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
Linear Mold Shrinkage, Flow 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Procedure A; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 82.0 MPa
11900 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 9.0 %
9.0 %
Type I, 51 mm/min; ASTM D638
Flexural Strength 115 MPa
16700 psi
Flexural Modulus 5.03 GPa
730 ksi
Izod Impact, Notched 0.800 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
1.50 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Izod Impact, Unnotched 3.40 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
6.37 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 162 °C

@Thickness 3.18 mm
324 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm

@Thickness 0.0591 in
ALL; UL 94
Processing Properties Metric English Comments
Mold Temperature 16.0 - 50.0 °C
60.8 - 122 °F
Descriptive Properties Value Comments
Appearance Black
Features Chemically Coupled
General Purpose
Filler / Reinforcement Glass Fiber Reinforcement
Unspecified FillerReinfor., 30% Filler by Weight
Forms Pellets
Generic Material PP Homopolymer
Generic Name Polypropylene Homopolymer (PP Homopolymer)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
North America
South America
Uses Automotive Applications
Construction Applications
Consumer Applications
General Purpose
Industrial Applications