Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 151 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 6.35 mm
304 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne LubriOne™ AT-000/18T 2S Acetal (POM) Copolymer
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 6.35 mm
304 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne LubriOne™ AT-000/20T Black Acetal (POM) Copolymer
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 3.18 mm
304 °F

@Thickness 0.125 in
Annealed; ASTM D648
PolyOne Maxxam™ PPC-10G Black Polypropylene Copolymer (PP Copolymer)
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 3.18 mm
304 °F

@Thickness 0.125 in
Annealed; ASTM D648
PolyOne Maxxam™ PPC-10G Nat Polypropylene Copolymer (PP Copolymer)
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 6.40 mm
304 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics Lexan® 3433R PC
30% GR, provides improved mechanical properties. UV-stabilized. Internal mold release.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP FARADEX KS002E Acetal Copolymer (Europe-Africa-Middle East)
LNP* FARADEX* KS002E is a compound based on Acetal Copolymer resin containing Stainless Steel Fiber. Added features include: EMI/RFI Shielding, Electrically Conductive, Easy Molding.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C

@Thickness 3.20 mm
304 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly (Asia Pacific)
LNP* Lubricomp* KP004L is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific)
LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11
LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ASTM D648
Samyang Trirex® 3025GNH15 Polycarbonate, Reinforced Flame Retardancy, Non-Halogen
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025GNH15 is a reinforced, flame retardant, non-halogen grade.Applications: LCD Panel ..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ASTM D648
Samyang Trirex® 3500G20 Polycarbonate, 20% Glass Reinforced
TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75
Teijin Panlite® GV-3430R High Flame Retardancy, Glass Fiber Reinforced Polycarbonate Resin
GF 30% reinforced, improved flame retardance and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecis..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1/-2
Unitika A1030BRL PA6, Dry
Information provided by Unitika Ltd.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
303 °F
ASTM D648
Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene
Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ASTM D648
Cheng Yu Plastic ML3430 PC, 30% Glass Fiber
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
Covestro Apec® HT KU 1-9333 High-Heat Polycarbonate
Transparent and opaque shades possible, UV-stabilized.Applications: Lighting, automotive and household goods, light covers.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Bf
Eurostar Staramide PX08000 PA6, Impact Modified, Injection Molded
Staramide PX08000 is an Impact Modified Polyamide 6 Injection Molding Resin (also known as Star X 2006)Information provided by Eurostar.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ASTM D648
Entec Hypro™ PPC-GF40 Natural Impact Polypropylene, 40% Glass Reinforced
Information provided by Entec
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ASTM D648
Aclo Accutech Polypropylene Homopolymer HP0339G10M20CL Glass/Mineral Reinforced Coupled
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Celcon® M90-45XAP® POM, Specialty
Celcon« acetal copolymer grade M90-45XAP« is a UV resistant, low emission version, medium viscosity polymer providing optimum performance in general purpose injection molding primarily for the in..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Hostaform® LX90Z POM, UV Resistant
Hostaform« LX90Z specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is t..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Hostaform® S 9362 POM, Impact Modified
Hostaform« acetal copolymer grade S 9362 is an impact modified grade for applications requiring improved impact. Hostaform« S 9362 provides good impact strength while improving modulus and weld ..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Hostaform® S 9362 XAP² ™ POM, Impact Modified
Preliminary Data SheetInformation provided by Celanese
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Hostaform® S 9362 XAP2 ™ POM, Impact Modified
Preliminary Data SheetDrying is suggested to help achieve low emission performance and to counter if material has contacted moisture through improper storage and handling.Information provided by Cel..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ASTM D648
A. Schulman ComAlloy Comtuf® 608 Nylon 6/12, Impact Modified
Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75 -1 & -2 flat
Asahi Kasei Tenac® 4012 Homopolymer Acetal Resin
Medium viscosity grade, with reduced stiffness and increased elongation through addition of special polymersInformation provided by Asahi Kasei Corporation.
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75
Teijin Panlite® G-3430R Glass Fiber Reinforced Polycarbonate Resin
GF 30% reinforced and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machinery components th..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Hostaform® S 9362 POM, Impact Modified  (Unverified Data**)
Hostaform® acetal copolymer grade S 9362 is an impact modified grade for applications requiring improved impact. Hostaform® S 9362 provides good impact strength while improving modulus and weld ..
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
ISO 75-1, -2
Celanese Hostaform® S 9362 XAP² ™ POM, Impact Modified  (Unverified Data**)
Preliminary Data SheetImpact modified, improved modulus and weld line, low emissionInformation provided by Celanese
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
304 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Thermocomp MF0069S PP
LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi..