SABIC Innovative Plastics LNP Thermotuf PX08000 PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermotuf PX08000 PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOTUF* PX08000 is a compound based on PA6 resin containing Impact Modifier. Added features include : High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 2.2 % @Temperature 23.0 °C, Time 86400 sec |
2.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 6.7 % | 6.7 % | Flexural Strain, 2 mm/min; ISO 178 |
| Elongation at Yield | 3.9 % | 3.9 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 102 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 99.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Oceanchem Group Xanthan Gum Oil Drilling Grade
- PSM Industries Pacific Sintered Metals Bronze BT-121-R Powdered Metal
- Reliance Industries LLDPE film - 1 MI O-LLDPE films
- Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Skamol Group Moler 10 Aggregate Insulation
- SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP
- Chase Plastics CP Pryme® N100L (COND, 50% RH) Nylon 6, Internally Lubricated
- Eurostar Staramide RF004XXC PA6, 20% Glass Fiber Filled, Injection Molded
- 3M Scotchcal™ 3662 Graphic Film
- Anderman Ceramics EM60P Sillimanite
Copyright © lookpolymers.com All Rights Reserved