SABIC Innovative Plastics LNP FARADEX KS002E Acetal Copolymer (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Steel Filled
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP FARADEX
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP FARADEX KS002E Acetal Copolymer (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* FARADEX* KS002E is a compound based on Acetal Copolymer resin containing Stainless Steel Fiber. Added features include: EMI/RFI Shielding, Electrically Conductive, Easy Molding.

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in³	ISO 1183
Water Absorption	0.31 % @Time 86400 sec	0.31 % @Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.025 cm/cm	0.025 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	51.0 MPa	7400 psi	5 mm/min; ISO 527
Elongation at Yield	7.8 %	7.8 %	5 mm/min; ISO 527
Tensile Modulus	2.80 GPa	406 ksi	1 mm/min; ISO 527
Flexural Yield Strength	80.0 MPa	11600 psi	2 mm/min; ISO 178
Flexural Modulus	2.60 GPa	377 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	30.0 kJ/m²	14.3 ft-lb/in²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	151 °C	304 °F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	84.0 °C	183 °F	Flatw 80104 sp=64mm; ISO 75/Af

Electrical Properties	Metric	English	Comments
Surface Resistance	100 - 10000 ohm	100 - 10000 ohm	ASTM D257
Shielding Effectiveness	35 - 50 dB @Thickness 3.00 mm	35 - 50 dB @Thickness 0.118 in	SABIC Method