Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 18.3 - 19.3 µm/m-°C @Temperature 20.0 - 300 °C |
10.2 - 10.7 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 18.3 - 19.3 µm/m-°C @Temperature 20.0 - 300 °C |
10.2 - 10.7 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition T7 Heat Treatment Condition T7 (Quenching in water at RT)Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allo.. |
|||
CTE, linear | 18.3 - 19.3 µm/m-°C @Temperature 20.0 - 300 °C |
10.2 - 10.7 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition T6 Heat Treatment Condition T6 (Quenching in water at RT)Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allo.. |
|||
CTE, linear | 18.3 µm/m-°C @Temperature 20.0 - 1093 °C |
10.2 µin/in-°F @Temperature 68.0 - 1999 °F |
|
ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, 1149°C (2100°F) Solution Treated, UNS N06601 Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increa.. |
|||
CTE, linear | 18.3 µm/m-°C @Temperature 20.0 - 1093 °C |
10.2 µin/in-°F @Temperature 68.0 - 1999 °F |
|
ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, Annealed at 982°C (1800°F), UNS N06601 Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increa.. |