ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, 1149°C (2100°F) Solution Treated, UNS N06601

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, 1149°C (2100°F) Solution Treated, UNS N06601.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increased chromium, an aluminum content which together provide outstanding resistance to oxidation. In addition, AL 601 alloy has good resistant to environments containing carbon and sulfur and this alloy resists aqueous corrosion. The AL 601 alloy is used in aerospace applications, for heat and chemical processing equipment, and in power generation, pollution control and heat treating applications. Forming, machining and welding properties are similar to those of stable austenitic stainless steels.Information provided by Allegheny Ludlum
Physical Properties Metric English Comments
Density 8.05 g/cc
0.291 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell B 70
70
Typical
Tensile Strength, Ultimate 670 MPa
97200 psi
Typical
Tensile Strength, Yield 250 MPa
36300 psi
Typical
Elongation at Break 55 %
55 %
typical in 2"
Reduction of Area 55 %
55 %
Typical
Modulus of Elasticity 205 GPa
29700 ksi
Charpy Impact 175 J
129 ft-lb
Typical
Thermal Properties Metric English Comments
CTE, linear 11.0 µm/m-°C

@Temperature 27.0 °C
6.11 µin/in-°F

@Temperature 80.6 °F
14.6 µm/m-°C

@Temperature 20.0 - 315 °C
8.11 µin/in-°F

@Temperature 68.0 - 599 °F
15.3 µm/m-°C

@Temperature 20.0 - 538 °C
8.50 µin/in-°F

@Temperature 68.0 - 1000 °F
18.3 µm/m-°C

@Temperature 20.0 - 1093 °C
10.2 µin/in-°F

@Temperature 68.0 - 1999 °F
Specific Heat Capacity 0.460 J/g-°C
0.110 BTU/lb-°F
Maximum Service Temperature, Air 1093 °C
1999 °F
High oxidation resistance due to tenacious oxide film formation.
Component Elements Properties Metric English Comments
Aluminum, Al 1.35 %
1.35 %
Carbon, C 0.050 %
0.050 %
Chromium, Cr 23 %
23 %
Copper, Cu 0.25 %
0.25 %
Iron, Fe 14.1 %
14.1 %
Manganese, Mn 0.50 %
0.50 %
Nickel, Ni 60.5 %
60.5 %
Silicon, Si 0.25 %
0.25 %
Sulfur, S 0.0050 %
0.0050 %
Electrical Properties Metric English Comments
Magnetic Permeability 1.02
1.02