- Polymer Property : Transformation Temperature = -18.0 °C
Polymer Property : Transformation Temperature = -18.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2110Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2110Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2121 Fluoroelastomer 3M™ Dyneon™ Flouroelastomer FC 2121 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2123 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2123 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2144 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2144 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2145 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2145 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2152 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2152 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2170 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2170 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2174 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2174 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2176 Fluoroelastomer Composition: di-polymer of vinylidene fluoride and hexafluoropropyleneAbility for fast cure cycles with excellent processing safetyMedium viscosityProcess targets: compression and transfer molding, .. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2178 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2178 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2179 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2179 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2230 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2230 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2260 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2260 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2261Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2261Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5620Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5620Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5621 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5621 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5623 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5623 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5641Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5641Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5642 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5642 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5643Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5643Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5660Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5660Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FG 5661 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FG 5661 can be compounded using standard water cooled internal mixers or two-roll mills. The “dry” ingredients should be blended before adding to the masticated gum. .. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FG 5690Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FG 5690Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2120 Fluoroelastomer 3M™ Dyneon™ Flouroelastomer FC 2120 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2180 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2180 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2181 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2181 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FE 5610 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5610 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2177D Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2177D can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2161X Fluoroelastomer
(discontinued **) Composition: di-polymer of vinylidene fluoride and hexafluoropropyleneMedium viscosityProcess targets: compression and transfer molding, and calenderingProprietary incorporated cure technologyExcell.. |
|||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
| 3M Dyneon™ FC 2173 Fluoroelastomer
(discontinued **) Composition: di-polymer of vinylidene fluoride and hexafluoropropyleneLow viscosityProcess targets: compression moldingProprietary incorporated cure technologyExcellent mold flow and mold release ch.. |
|||