Polymer Property : CTE, linear, Parallel to Flow = 33.3 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 50.0 - 100 °C	27.8 - 33.3 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 50.0 - 100 °C	27.8 - 33.3 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4355 G5 25% Glass Filled PA6/6T (Dry) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Dry) Description: 25% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4355 G7 BK 00564 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Dry) Description: 30% glass-fiber reinforced, impact-modified product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechan..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Dry) Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resi..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® KR 4365 G5 BK 00100 35% Glass Filled PA6/6T FR (Dry) Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resi..
CTE, linear, Parallel to Flow	50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 53752
BASF Ultradur® B 4406 PBT Description: Is a PBT, flame-retardant injection-molding grades, unreinforced for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and lighting compo..
CTE, linear, Parallel to Flow	40.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C	22.2 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3UGM210 GR 22866 10/50% Glass/Mineral Filled PA6 FR (Dry) Description: Halogen- and phosphorus-free injection-molding grade with very high rigidity, low smoke density and outstanding electrical properties.Information provided by BASF