BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 30% glass-fiber reinforced, impact-modified product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F], for instance, for automotive plug-in connectors.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 4.0 - 5.0 %
4.0 - 5.0 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 0.60 - 1.0 %
0.60 - 1.0 %
23°C; 50% RH; ISO 62
Viscosity Measurement 130
130
ISO 307
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
restricted
Linear Mold Shrinkage, Flow 0.0036 cm/cm
0.0036 in/in
TM=320°C, TW=100°C
0.0040 cm/cm
0.0040 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 165 MPa
23900 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 9.30 GPa
1350 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) 23.0 kJ/m²

@Temperature 23.0 °C
10.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 9.50 J/cm²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.90 J/cm²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 - 60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
27.8 - 33.3 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
13.9 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 295 °C
563 °F
DIN 53765
Maximum Service Temperature, Air 130 °C
266 °F
for 50% loss of tensile strength after 20000hr
160 °C
320 °F
for 50% loss of tensile strength after 5000hr
270 °C
518 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1/-2
Decomposition Temperature >= 350 °C
>= 662 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Dielectric Constant 4.3

@Frequency 1.00 Hz
4.3

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.030

@Frequency 1.00e+6 Hz
0.030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 300 °C
572 °F
Feed Zone
Zone 2 310 °C
590 °F
Compression
Zone 3 320 °C
608 °F
Metering-zone
Zone 4 320 °C
608 °F
Nozzle
Melt Temperature 310 - 330 °C
590 - 626 °F
Injection-molding/Extrusion
320 °C
608 °F
Optimal
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Injection-molding
100 °C
212 °F
Optimal
Drying Temperature 110 °C
230 °F
Dry Time 8 hour
8 hour
Moisture Content <= 0.030 %
<= 0.030 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 00564
Commercial Status Europe
Ignition Temperature >470°C
ASTM D1929
Peripheral screw speed <0.3 m/s