BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F], for instance, for automotive valve housings.Information provided by BASF
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Water Absorption 4.3 - 5.3 %
4.3 - 5.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 0.80 - 1.2 %
0.80 - 1.2 %
23°C; 50% RH; ISO 62
Viscosity Measurement 130
130
ISO 307
Linear Mold Shrinkage 0.0033 cm/cm
0.0033 in/in
restricted
Mechanical Properties Metric English Comments
Tensile Strength 40.0 MPa

@Strain 2.00 %,
Temperature 150 °C
 5800 psi

@Strain 2.00 %,
Temperature 302 °F
 5mm/min
50.0 MPa

@Strain 2.00 %,
Temperature 100 °C
 7250 psi

@Strain 2.00 %,
Temperature 212 °F
 5mm/min
60.0 MPa

@Strain 6.00 %,
Temperature 150 °C
 8700 psi

@Strain 6.00 %,
Temperature 302 °F
 5mm/min
65.0 MPa

@Strain 9.00 %,
Temperature 150 °C
 9430 psi

@Strain 9.00 %,
Temperature 302 °F
 5mm/min
75.0 MPa

@Strain 6.00 %,
Temperature 100 °C
 10900 psi

@Strain 6.00 %,
Temperature 212 °F
 5mm/min
80.0 MPa

@Strain 9.00 %,
Temperature 100 °C
 11600 psi

@Strain 9.00 %,
Temperature 212 °F
 5mm/min
100 MPa

@Strain 2.00 %,
Temperature 80.0 °C
 14500 psi

@Strain 2.00 %,
Temperature 176 °F
 5mm/min
110 MPa

@Strain 1.00 %,
Temperature 60.0 °C
 16000 psi

@Strain 1.00 %,
Temperature 140 °F
 5mm/min
120 MPa

@Strain 3.00 %,
Temperature 80.0 °C
 17400 psi

@Strain 3.00 %,
Temperature 176 °F
 5mm/min
125 MPa

@Strain 5.00 %,
Temperature 80.0 °C
 18100 psi

@Strain 5.00 %,
Temperature 176 °F
 5mm/min
160 MPa

@Strain 2.00 %,
Temperature 60.0 °C
 23200 psi

@Strain 2.00 %,
Temperature 140 °F
 5mm/min
175 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 25400 psi

@Strain 1.00 %,
Temperature 73.4 °F
 5mm/min
200 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 29000 psi

@Strain 2.00 %,
Temperature 73.4 °F
 5mm/min
Tensile Strength, Yield 210 MPa
30500 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 12.0 GPa
1740 ksi
ISO 527-1/-2
5.00 GPa

@Temperature 140 °C
 725 ksi

@Temperature 284 °F
 ISO 527
9.00 GPa

@Temperature 80.0 °C
 1310 ksi

@Temperature 176 °F
 ISO 527
12.0 GPa

@Temperature 0.000 °C
 1740 ksi

@Temperature 32.0 °F
 ISO 527
12.0 GPa

@Temperature 40.0 °C
 1740 ksi

@Temperature 104 °F
 ISO 527
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 - 60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 27.8 - 33.3 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
CTE, linear, Transverse to Flow 15.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 8.33 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
Specific Heat Capacity 1.30 J/g-°C
0.311 BTU/lb-°F
Thermal Conductivity 0.280 W/m-K
1.94 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 295 °C
563 °F
DIN 53765
Maximum Service Temperature, Air 135 °C
275 °F
for 50% loss of tensile strength after 20000hr
160 °C
320 °F
for 50% loss of tensile strength after 5000hr
270 °C
518 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
2.00e+9 ohm-cm

@Temperature 140 °C
 2.00e+9 ohm-cm

@Temperature 284 °F
 IEC 60093
6.00e+10 ohm-cm

@Temperature 120 °C
 6.00e+10 ohm-cm

@Temperature 248 °F
 IEC 60093
1.00e+13 ohm-cm

@Temperature 100 °C
 1.00e+13 ohm-cm

@Temperature 212 °F
 IEC 60093
1.00e+15 ohm-cm

@Temperature 80.0 °C
 1.00e+15 ohm-cm

@Temperature 176 °F
 IEC 60093
5.00e+15 ohm-cm

@Temperature 60.0 °C
 5.00e+15 ohm-cm

@Temperature 140 °F
 IEC 60093
5.00e+15 ohm-cm

@Temperature 20.0 °C
 5.00e+15 ohm-cm

@Temperature 68.0 °F
 IEC 60093
1.00e+16 ohm-cm

@Temperature 40.0 °C
 1.00e+16 ohm-cm

@Temperature 104 °F
 IEC 60093
Dielectric Constant 4.2

@Frequency 1.00 Hz
 4.2

@Frequency 1.00 Hz
 IEC 60250
Dissipation Factor 0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe