Toyobo GLAMIDE® T-803 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-803 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-803 is a hard type, non-reinforced Nylon-6 used in high-cycles.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | Absolute Drying; ASTM-D792 |
| Water Absorption | 1.8 % | 1.8 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 3.5 % | 3.5 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm @Thickness 1.00 mm |
0.0040 - 0.0070 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.012 - 0.014 cm/cm @Thickness 3.00 mm |
0.012 - 0.014 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 44 g/10 min | 44 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
Practical Use (Water Absorption 3.5%); ASTM-D638 |
| 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 45.0 MPa @Temperature 23.0 °C |
6530 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 3.5%); ASTM-D638 | |
| 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 3.5%); ASTM-D638 | |
| 120 MPa @Temperature -40.0 °C |
17400 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 30 % | 30 % | Absolute Drying; ASTM-D638 |
| >= 200 % | >= 200 % | Practical Use (Water Absorption 3.5%); ASTM-D638 | |
| Flexural Strength | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
Practical Use (Water Absorption 3.5%); ASTM-D790 |
| 49.0 MPa @Temperature 23.0 °C |
7110 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 3.5%); ASTM-D790 | |
| 55.0 MPa @Temperature 80.0 °C |
7980 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 113 MPa @Temperature 23.0 °C |
16400 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 125 MPa @Temperature -40.0 °C |
18100 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 3.5%); ASTM-D790 | |
| 140 MPa @Temperature -40.0 °C |
20300 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 0.500 GPa @Temperature 80.0 °C |
72.5 ksi @Temperature 176 °F |
Practical Use (Water Absorption 3.5%); ASTM-D790 |
| 0.900 GPa @Temperature 80.0 °C |
131 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 1.10 GPa @Temperature 23.0 °C |
160 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 3.5%); ASTM-D790 | |
| 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 3.60 GPa @Temperature -40.0 °C |
522 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 3.5%); ASTM-D790 | |
| 4.00 GPa @Temperature -40.0 °C |
580 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 85.0 MPa | 12300 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 0.300 J/cm @Temperature -40.0 °C |
0.562 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.450 J/cm @Temperature -40.0 °C |
0.843 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 3.5%); ASTM-D256 | |
| 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 3.90 J/cm @Temperature 23.0 °C |
7.31 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 3.5%); ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 5.0 | 5.0 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 83.0 µm/m-°C | 46.1 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 - 1.00e+9 ohm-cm | 1.00e+8 - 1.00e+9 ohm-cm | Practical Use (Water Absorption 3.5%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Constant | 3.8 @Frequency 1000 Hz |
3.8 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| 8.0 @Frequency 1000 Hz |
8.0 @Frequency 1000 Hz |
Practical Use (Water Absorption 3.5%); ASTM-D150 | |
| Dielectric Strength | 12.0 kV/mm @Thickness 2.00 mm |
305 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 3.5%); ASTM-D149 |
| 18.0 kV/mm @Thickness 2.00 mm |
457 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Arc Resistance | 105 sec | 105 sec | Practical Use (Water Absorption 3.5%); ASTM-D495 |
| 125 sec | 125 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Injection Pressure | 30.0 - 40.0 MPa | 4350 - 5800 psi |