Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Puncture Energy | 1.80 - 10.6 J | 1.33 - 7.82 ft-lb | Average value: 4.07 J Grade Count:4 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Puncture Energy | 1.80 - 1.80 J @Temperature -30.0 - -30.0 °C |
1.33 - 1.33 ft-lb @Temperature -22.0 - -22.0 °F |
Average value: 1.80 J Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | Exxon Mobil Method |
ExxonMobil Exceed™ 1018 DA Blown Film Resin
(discontinued **) Exceed 1018 resins are hexene copolymer produced using ExxonMobil Chemicals Exxpol® Technology. Films made from 1018 resins have outstanding tensile properties and impact and puncture toughness. .. |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | Exxon Mobil Method |
ExxonMobil Exceed™ 1018 FA Blown Film Resin
(discontinued **) Exceed 1018 resins are hexene copolymer produced using ExxonMobil Chemicals Exxpol® Technology. Films made from 1018 resins have outstanding tensile properties and impact and puncture toughness. .. |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | ISO 6603-2 |
Lanxess Durethan® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
Puncture Energy | 1.80 J @Temperature -30.0 °C |
1.33 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
Lanxess Durethan® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
Puncture Energy | 1.80 J @Temperature -30.0 °C |
1.33 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
Lanxess Durethan® BKV 15 H2.0 901510 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
Puncture Energy | 1.80 J @Temperature -30.0 °C |
1.33 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | ISO 6603-2 |
Lanxess Pocan® B 4225 000000 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding, flame retardant |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | ISO 6603-2 |
Lanxess Pocan® BF 4225 000000 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding, flame retardant |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | Exxon Mobil Method |
ExxonMobil Exceed™ 1018 EA Blown Film Resin
(discontinued **) Exceed 1018 resins are hexene copolymer produced using ExxonMobil Chemicals Exxpol® Technology. Films made from 1018 resins have outstanding tensile properties and impact and puncture toughness. .. |
|||
Puncture Energy | 1.80 J @Temperature -30.0 °C |
1.33 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
Lanxess Pocan® TS 3220 901510 PBT + PET, 20% Glass Fiber PBT+PET, 20% glass fibers, injection molding, impact modified, low tendency to warp, improved surface finish |
|||
Puncture Energy | 1.80 - 1.80 J @Temperature -30.0 - -30.0 °C |
1.33 - 1.33 ft-lb @Temperature -22.0 - -22.0 °F |
Average value: 1.80 J Grade Count:1 |
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Puncture Energy | 1.80 J | 1.33 ft-lb | Exxon Mobil Method |
ExxonMobil Exceed™ 1018 EB Blown Film Resin
(discontinued **) Exceed 1018 resins are hexene copolymer produced using ExxonMobil Chemicals Exxpol® Technology. Films made from 1018 resins have outstanding tensile properties and impact and puncture toughness. .. |