- Lanxess Pocan® BF 4225 000000 PBT, 20% Glass Fiber
Lanxess Pocan® BF 4225 000000 PBT, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® BF 4225 000000 PBT, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 20% glass fibers, injection molding, flame retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.595 g/cc | 0.05762 lb/in³ | ISO 1183 |
| Viscosity Test | 97 cm³/g | 97 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 260 °C |
30 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-1/-2 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Puncture Energy | 1.80 J | 1.33 ft-lb | ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 126 °C | 259 °F | ISO 75-1/-2 |
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Lubricants | ||
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GFHMR,07-080,GF20; ISO 1043-PBT GF FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nye Lubricants 789DM (RL) Synthetic Oil
- Rogers Corporation Poron® 4701-30-25 Urethane Foam, Very Soft
- S&E Specialty Polymers TufTech™ GA-1038 Natural 85 PVC Compound
- Premix Premi-Glas® 2205-30 CR-SX Fiberglass Reinforced SMC
- Solvay Engineered Polymers SEQUEL® 1783 Engineered Polyolefin (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000MDL Nylon 6/6 (discontinued **)
- Lanxess Durethan® BC 600 HTS DUSXBL 900116 Nylon 6, Impact Modified
- SABIC Innovative Plastics Ultem 2313 PEI
- Arlon Flexible Silicon Insulation with Fiberglass Substrate (56493F031)
- PolyOne Synprene® RT-3810M Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved