Polymer Property : Flexural Modulus = 841 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 5.80 GPa
841 ksi
STN EN ISO 178
Plastcom SLOVAMID 6 GF 15 T 25 Polyamide 6, 15% Glass Fiber, 25% Micronized Talc
FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form / no screw after co..
Flexural Modulus 5.80 GPa
841 ksi
Plastcom SLOVAMID 6 GF 20 TS PA6, 20% glass fibre, thermal stability
FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre, heat stabilized . Application: impacted mouldings and mouldings with high strength applied in automotive, electrica..
Flexural Modulus 5.80 GPa
841 ksi
Plastcom SLOVAMID 66 GF 15 GB 25 TS PA66, 15% glass fibre, 25% glass beads
FeaturesPA 66 chemically reinforced with 15 % glass fibre and with the content of 25% glass beads, thermo stable. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical p..
Flexural Modulus 5.80 GPa

@Temperature 23.0 °C
841 ksi

@Temperature 73.4 °F
ISO 178
Polykemi AB POLYfill PPH GF12030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
Information provided by Polykemi AB
Flexural Modulus 5.80 GPa
841 ksi
STN EN ISO 178
Plastcom SLOVAMID 6 GF 20 Polyamide 6, 20% Glass Fiber
FeaturesPA 6 for injection moulding, chemically coupled with 20% glass fiber. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and con..
Flexural Modulus 5.80 GPa

@Temperature 23.0 °C
841 ksi

@Temperature 73.4 °F
ISO 178
DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)
Sorona® 3015GV NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness and sur..
Flexural Modulus 5.80 GPa

@Temperature 23.0 °C
841 ksi

@Temperature 73.4 °F
ISO 178
DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**
Sorona® FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) formulated to be food c..
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP BG004 SAN (Europe-Africa-Middle East)
LNP* LUBRICOMP* BG004 is a compound based on Styrene Acrylonitril resin containing Graphite. Added features include: Internally Lubricated.
Flexural Modulus 5.80 GPa
841 ksi
ASTM D790
Kotec Carbotex KG-30F15 Polycarbonate, Wear Resistant, 30% Glass Fiber Reinforced
Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Non-frictionApplications: OA equipment, Communications, Precision parts, Machineries, E & E partsInformation p..
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Flexural Modulus 5.80 GPa
841 ksi
d.a.m., 2 mm/min; ISO 178-A
Lanxess Durethan® BG 30 X W1 000000 Nylon 6, Glass Fiber Reinforced
PA 6, 30% glass fibers/glass spheres, injection molding, low tendency to warp, weather stabilizedInformation provided by LANXESS.
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, DRY
Description: Copolyamide 66/6, reinforced with 20% of glass fiber, for injection molding, heat stabilized with improved UV ageing resistanceAvailable in: Asia Pacific and EuropeProduct Applications:..
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66
LNP* LUBRICOMP* RFL33 is a compound based on Nylon 66 resin containing 15% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Asia Pacific)
LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Modulus 5.80 GPa
841 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® VX5022 PBT (Europe-Africa-Middle East)
VALOX VX5022 is a 20% glass fibre reinforced PBT+PC blend with low warpage characteristics. This grade is 5021 with reduced warpage.
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP JF004Z PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF004Z is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: HV.
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP PCAF04FRHH PC+ABS (Europe-Africa-Middle East)
LNP* THERMOCOMP* PCA04FRHH is a 20 % glass reinforced PC+ABS blend without chlorinated or brominated flame retardants. LNP* THERMOCOMP* complies with the material requirements as specified in TCO'99..
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East)
glas, mineral filled PPE
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS (Europe-Africa-Middle East)
LNP* THERMOCOMP* ZF004 is a compound based on PPE+PS Blend resin containing Glass Fiber.
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
Polyram PlusTek PA301G2 Nylon 6.6 for Injection Molding, 10% Glass Fiber Reinforced, Heat Stabilized
Heat stabilized, 10% Glass fiber reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
Flexural Modulus 5.80 GPa

@Temperature 120 °C
841 ksi

@Temperature 248 °F
ISO 178
DSM Stanyl® TE200F8 PA46-GF40
40% Glass Reinforced, Heat Stabilized, for E&E applications
Flexural Modulus 5.80 GPa
841 ksi
cond; ISO 178
DSM Stanyl® TS241B3 PA46-CF15
15% Carbon Reinforced, Lubricated
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT)
15% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3015GV NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on pol..
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
Eurostar Staramide BG4H PA6, 20% Glass Filled, Injection Molded
BG4H is a Heat Stabilized, 20% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Flexural Modulus 5.80 GPa
841 ksi
ISO Data
BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Dry)
Ultramid 1403-2 NF3001 is a 13% glass reinforced, heat stabilized injection molding PA6/6.
Flexural Modulus 5.80 GPa
841 ksi
ASTM D790
Ashley Polymers Ashlene® P123 PBT Polyester, 15% Glass Reinforced
PBT polyester with 15% glass reinforcement.Data provided by the manufacturer
Flexural Modulus 5.80 GPa
841 ksi
Plastcom SLOVAMID 6 NG GF 20 PA6, 20% glass fibre
FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and..
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
Celanese THERMX CG023 PCT, 20% Glass Reinforced
Thermx« CG023 is a 20% glass fiber reinforced polycyclohexylenedimethylene terephthalate for injection molding.Information provided by Celanese
Flexural Modulus 5.80 GPa
841 ksi
cond; ISO 178
DSM Stanyl® TS200B3 PA46-CF15
15% Carbon Reinforced
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PX1786G PPE+HIPS (Europe-Africa-Middle East)
NORYL PX1786G is a 30 % glass filled material with a Vicat B/120 of 160 °C.