SABIC Innovative Plastics Noryl GFN1420V PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl GFN1420V PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designed to have higher flow compared to Noryl GFN1520V resin. Noryl GFN1420V resin will be certified for potable water applications up to 85C in Europe and North America in limited colors.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D 792
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.060 %
0.060 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %

@Temperature 23.0 °C
0.20 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 11 g/10 min

@Load 5.00 kg,
Temperature 280 °C
11 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D 1238
23 g/10 min

@Load 10.0 kg,
Temperature 280 °C
23 g/10 min

@Load 22.0 lb,
Temperature 536 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
5 mm/min; ISO 527
109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 105 MPa
15200 psi
5 mm/min; ISO 527
109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D 638
2.5 %
2.5 %
5 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D 638
2.5 %
2.5 %
5 mm/min; ISO 527
Tensile Modulus 6.40 GPa
928 ksi
1 mm/min; ISO 527
6.50 GPa
943 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 155 MPa
22500 psi
2 mm/min; ISO 178
159 MPa
23100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 5.80 GPa
841 ksi
2 mm/min; ISO 178
5.90 GPa
856 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.920 J/cm

@Temperature -30.0 °C
1.72 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
0.980 J/cm

@Temperature 23.0 °C
1.84 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.10 J/cm

@Temperature -30.0 °C
9.55 ft-lb/in

@Temperature -22.0 °F
ASTM D 4812
5.10 J/cm

@Temperature 23.0 °C
9.55 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Impact Test 17.0 J

@Temperature 23.0 °C
12.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
132 °C

@Thickness 3.20 mm
270 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 135 °C
275 °F
Rate B/50; ASTM D 1525
135 °C
275 °F
Rate B/50; ISO 306
141 °C
286 °F
Rate B/120; ISO 306