SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow PPE+PS+PA for under-the-hood and electrical applications. With mold releaseThis data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D 792
Water Absorption at Saturation 4.2 %

@Temperature 23.0 °C
4.2 %

@Temperature 73.4 °F
ASTM D 570
Linear Mold Shrinkage, Flow 0.013 - 0.016 cm/cm

@Thickness 3.20 mm
0.013 - 0.016 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.010 - 0.013 cm/cm

@Thickness 3.20 mm
0.010 - 0.013 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 5.0 g/10 min

@Load 1.20 kg,
Temperature 280 °C
5.0 g/10 min

@Load 2.65 lb,
Temperature 536 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
45 g/10 min

@Load 5.00 kg,
Temperature 280 °C
45 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 30 %
30 %
50 mm/min; ISO 527
53 %
53 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527
11.4 %
11.4 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 0.810 GPa
117 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 85.0 MPa
12300 psi
2 mm/min; ISO 178
98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
2.36 GPa
342 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.02 J/cm

@Temperature 23.0 °C
3.78 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
20.0 kJ/m²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 40.0 J

@Temperature 23.0 °C
29.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 68.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
188 °C

@Thickness 3.20 mm
370 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 148 °C

@Thickness 3.20 mm
298 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 190 °C
374 °F
Rate B/50; ISO 306
195 °C
383 °F
Rate B/120; ISO 306
242 °C
468 °F
Rate B/50; ASTM D 1525
245 °C
473 °F
Rate A/50; ISO 306