Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.586 GPa | 85.0 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
Network Polymers NPP 50-0548 Description: High Density Polyethylene (HDPE)Information provided by Network Polymers Inc. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
Quadrant EPP Symalit® PFA Tetrafluoroethylene-perfluoroalkylvinylether (ASTM Product Data Sheet) |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
Quadrant EPP TIVAR® SuperPlus UHMW-PE, Glass-filled Cross-linked & Heat Stabilized Extreme Wear Resistant (ASTM Product Data Sheet) |
|||
Flexural Modulus | 0.586 - 2.62 GPa | 85.0 - 380 ksi | Average value: 1.24 GPa Grade Count:214 |
Overview of materials for High Density Polyethylene (HDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Blow Molding Grade". Each property range of values reported is minimum.. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
Global TPO-55D TPO Grade Data provided by Global Polymers Corporation. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
Chase Plastics CP Pryme® NN300STL (COND, 50% RH) Nylon 66 (Utility Grade), Super Toughened, Internally Lubricated Information provided by Chase Plastics. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene Information provided by A. Schulman. |
|||
Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |