- Polymer Property : Tensile Strength, Ultimate = 896 MPa
Polymer Property : Tensile Strength, Ultimate = 896 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Typical |
| PSM Industries PolyAlloys MIM-17-4PH sintered Stainless Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
| Tensile Strength, Ultimate | 896 MPa @Temperature 400 °C |
130000 psi @Temperature 752 °F |
|
| Kennametal Stellite Nucalloy® 453 High-Silicon Nickel-Base Hardfacing Alloy Applications include chemical control valves, nuclear globe valves, nuclear gate valves, nuclear sliding parts, and pressure bars for plywood cutters.Nucalloy® alloys are unique, patented, high-s.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Kinetics MIM 17-4PH Stainless Steel (As Sintered) Precipitation-hardening stainless steel. Offers a good balance between corrosion resistance and strength. Magnetic. Hardenable to various strength levels and hardness by varying the aging heat treat.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Annealed |
| Kinetics MIM F1537 (ASTM F1537) HIP and Heat Treat Most commonly used within the medical market on applications requiring these characteristics: Bio-compatibility Corrosion resistance High strength Nonmagnetic Wear resistance. Information prov.. |
|||
| Tensile Strength, Ultimate | >= 896 MPa | >= 130000 psi | |
| Kobe Steel KS6-2-4-2 Alpha Titanium Alloy, AMS 4976, Solution treated and aged Nominal Composition: Ti-6 Al-2 Sn-4 Zr-2 Mo Applications: Jet engine parts, engine valves.Features:Heat resistant. Information provided by Kobe Steel |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Meehanite K-295 Austempered Ductile Iron Type K-295 is used for applications such as gears requiring high contact rolling and tooth bending fatigue properties. Type K-295 also possess high fracture toughness impact strength. Excellent fo.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Stainless Steel 918-8) Cold Rolled butt joint |
| Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal Applications: Easy-Flo is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wettin.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Annealed |
| Latrobe MP35N® Alloy MP35N is a nickel-cobalt base alloy of the Multiphase alloy system that has a unique combination of properties - ultra high strength, toughness, ductility, and outstanding corrosion resistance. The .. |
|||
| Tensile Strength, Ultimate | 896 MPa @Temperature 316 °C |
130000 psi @Temperature 601 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Ultimate | >= 896 MPa | >= 130000 psi | |
| Materion Alloy M65 (C17465) Beryllium Copper Rod Alloy M65 (C17465) is a machinable, high-performance, copper beryllium rod alloy from Brush Wellman. M65 has excellent strength, conductivity, and resistance to elevated temperature stress relaxatio.. |
|||
| Tensile Strength, Ultimate | 896 - 1206 MPa | 130000 - 174900 psi | |
| Materion Beryllium Nickel Strip - Alloy 360 1/2 Hard Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedFormability Ratio, 90° Bend, Radius/Thickness (Good Way): 0.7Formability Ratio (bad Way).. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Tensile Strength, Ultimate | 896 - 1070 MPa | 130000 - 155000 psi | |
| Special Metals DURANICKEL® 301 (UNS N03301) Half-Hard Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Universal Wire Works 6Al-4V (AMS 4954) Titanium Alloy Filler Metal Universal 6Al-4V titanium alloy is often repaired with the gas tungsten arc or gas metal arc welding process, provided adequate inert gas shielding of the filler wire and deposited weld metal is pro.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| Universal Wire Works 6Al-4V (ELI) (AMS 4956) Titanium Alloy Filler Metal Universal titanium alloy 6Al-4V (ELI) is similar to type 6Al-4V in chemical analysis with the exception of Extra Low Interstitial gases (ELI). By controlling these contaminating gases the fracture t.. |
|||
| Tensile Strength, Ultimate | >= 896 MPa | >= 130000 psi | |
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, |
|||
| Tensile Strength, Ultimate | >= 896 MPa | >= 130000 psi | |
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, 4.00-6.00 in, Annealed, Per Mil-T-9047G; other specific form/thickness entries .. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| ECOMold 95 Copper Mold Material ECOMold® copper alloys (beryllium-free) are designed specifically for plastics industry applications. ECOMold® 95 has a superior combination of thermal conductivity, hardness, and tensile strengt.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| CMW® 3950 AMS-T-21014 ASTM B777 High Density Machinable Tungsten Uses: Radiation Shielding, High Mass, Gyro, Ordnance. Machinability is similar to gray iron.Information provided by CMW Inc. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | cold worked |
| CMW® ELKONIUM 34 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| AK Steel 17-7 PH® Precipitation Hardening Stainless Steel, Condition A AK Steel 17-7 PH® provides high strength and hardness, excellent fatigue properties, good corrosion resistance, good formability, and minimum distortion upon heat treatment. This alloy provides va.. |
|||
| Tensile Strength, Ultimate | 896 - 965 MPa | 130000 - 140000 psi | |
| Ametek AM 388™ Alloy (UNS C72650) TS01 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | Rm |
| Arcam ASTM F-75 Cobalt Chrome Alloy ASTM F-75 Cobalt Chromium alloys are widely used in orthopedic implants such as cemented total hip or knee arthroplasty as well as in metal-on-metal bearings in total hip arthroplasty. The alloys fe.. |
|||
| Tensile Strength, Ultimate | 896 MPa @Temperature 538 °C |
130000 psi @Temperature 1000 °F |
|
| Carpenter Custom 455® Stainless Steel, Condition H950 (Age Hardened 510°C) Data provided by Carpenter Technology Corporation.Recognizing the need for high-strength alloys with good corrosion resistance to atmospheric environments, the Carpenter Research Laboratory develope.. |
|||
| Tensile Strength, Ultimate | 896 MPa | 130000 psi | |
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| Tensile Strength, Ultimate | <= 896 MPa | <= 130000 psi | AMS 5542 annealed, strip and sheet |
| ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information.. |
|||
| Tensile Strength, Ultimate | 896 - 999 MPa | 130000 - 145000 psi | |
| Ametek AM 388™ Alloy (UNS C72650) TM08 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||