Polymer Property : Tensile Strength, Ultimate = 6.00 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	6.00 MPa	870 psi	500 mm/min (20 in./min.); Type IV Specimen; ASTM D638
Eastman 812A Polyethylene (discontinued **) Polyethylene 812A is a natural low density material with a 200 melt index. This high-flow formulation is used for specialty injection molding applications in the medical market.Unless otherwise not..
Tensile Strength, Ultimate	6.00 - 185 MPa	870 - 26800 psi	Average value: 86.9 MPa Grade Count:161
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb..
Tensile Strength, Ultimate	6.00 MPa	870 psi
Dow Corning HV 1520/40 40 Shore Hardness Conductive liquid silicone rubber with high tear strength, high electrical conductivity and fast cure speedInformation provided by Dow Corning
Tensile Strength, Ultimate	6.00 MPa	870 psi
Dow Corning SILASTIC® 9251/45 A&B KIT 45 Durometer, 2-part, 1 to 1 mix, off-white, Fabric Coating grade, Liquid Silicone Rubber.Information provided by Dow Corning
Tensile Strength, Ultimate	6.00 MPa	870 psi
Dow Corning SILASTIC® 9252/500P PARTS A&B Information provided by Dow Corning
Tensile Strength, Ultimate	6.00 - 15.0 MPa	870 - 2180 psi
ATG s.r.l. CO-ECO Epichlorohydrin Rubber
Tensile Strength, Ultimate	6.00 - 18.0 MPa	870 - 2610 psi
ATG s.r.l. EPDM Ethylene-Propylene Terpolymer
Tensile Strength, Ultimate	6.00 - 18.0 MPa	870 - 2610 psi
ATG s.r.l. EPM Ethylene-Propylene Copolymer
Tensile Strength, Ultimate	6.00 - 10.0 MPa	870 - 1450 psi
ATG s.r.l. FVMQ Fluorosilicone Rubber
Tensile Strength, Ultimate	6.00 - 9.00 MPa	870 - 1310 psi
ATG s.r.l. PVMQ Silicone Rubber